通过常规力学性能测试设备和SEM,XRD研究了回火温度和回火时间对贝氏体型非调质钢力学性能的影响.研究结果表明:在300～6000℃不同温度保温2h的回火处理后.屈服强度在350℃达到峰值,在450℃落到谷值;抗拉强度随回火温度的提高一直下降;硬度在550℃以上才明显下降;而冲击韧性在325℃达到峰值,在450℃落到谷值.在350℃不同时间回火后,屈服强度和抗拉强度并没有随回火时间的延长明显下降,而冲击韧性在保温2h时达最大值.之后急剧下降.
参考文献
| [1] | 许珞萍,邵光杰,李麟,张恒华.汽车轻量化用金属材料及其发展动态[J].上海金属,2002(03):1-7. |
| [2] | 彭瑶玮,何国伟.C、Si、N元素对非调质贝氏体钢的组织和强韧性的影响[J].热处理,2003(01):13-19. |
| [3] | Dongyu Liu;Bingzhe Bai;Hongsheng Fang .Effect of tempering temperature and carbide free bainite on the mechanical characteristics of a high strength low alloy steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):40-44. |
| [4] | X.D. Wang;B.X. Huang;Y.H. Rong;L. Wang .Microstructures and stability of retained austenite in TRIP steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):300-305. |
| [5] | Van Dijk N H;Butt A M;Zhao L et al.Thermal stability of retained austenite in TBIP steels studied by synchrotron X-ray diffraction during cooling[J].ACTA MATERIALIA,2005,53:5439-5447. |
| [6] | Bhadeshia H K D H;Waugh A R .[J].Acta Metallurgica,1982,30:775. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%