使用热力学软件FactSage计算固定CaO、MgO含量的MnO-SiO2-Al2O3渣系相图低熔点区(≤1 500℃),及固定MnO、MgO含量的CaO-SiO2-Al2O3渣系相图低熔点区；同时按照扫描电镜能谱分析得到的帘线钢盘条中夹杂物成分,用分析纯试剂配制夹杂物,测定其熔化温度,将其标在相图中相应位置,并与FactSage计算的熔点结果对比.结果表明,夹杂物熔化温度测定结果与FactSage计算结果基本相符,在此基础上,讨论了夹杂物熔点与变形状态的关系.
参考文献
| [1] | Malm S .On the precipitation of slag inclusions during solidification of high carbon steel deoxidized with aluminium and mish metal[J].Scandinavian Journal of Metallurgy,1976,15:248. |
| [2] | Bernard G;Ribound P V .Urbain G.Oxide inclusions plasticity[J].Rev Metall CIT,1981,78(05):421. |
| [3] | Jun Kawahara;Koji Tanabe;Toshio Banno.Advance of valve Spring Steel[J].Wire Journal International,1992(11):55-61. |
| [4] | 顾克井,魏军,蔡开科,王春怀.72A钢非金属夹杂物行为[J].北京科技大学学报,2003(01):26-29. |
| [5] | 何燕霖,李麟,吴晓春.计算热力学在钢中非金属夹杂物研究中的应用[J].上海金属,2004(01):1-6. |
| [6] | 董履仁;刘新华.钢中大型非金属夹杂物[M].北京:冶金工业出版社,1991:15-19. |
| [7] | Martin Gagne;Eric Thibault .Behaviour of inclusions during rolling of continuously cast billets[J].CIM Bulletin,1998,91(1021):98-103. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%