通过对 Fe 基非晶合金带材连续施加压力,测试其附近闭合回路电感变化,研究了Fe基非晶合金带材的电感式压磁效应。结果表明,通过测试 Fe基非晶合金带材附近闭合回路电感变化可用来测试和表征Fe基非晶合金带材的压磁性能；在f=1kHz时,Fe基非晶合金带材压磁性能稳定性好,随着压力的增大带材压磁性能升高,在同一压力情况下, Fe73.5 Cu1 Nb3 Si13.5 B9带材压磁性能优于 Fe78 Si9 B13带材；在f=100kHz 时,Fe73.5 Cu1 Nb3 Si13.5 B9带材压磁性能稳定性优于 Fe78 Si9 B13带材,并且 Fe73.5 Cu1 Nb3-Si13.5 B9带材在f=1kHz、压应力为0.69MPa 时具有最佳的压磁性能；在压应力<0.1 MP a 条件下,随着压应力增大,线圈电感值Ls 有一个剧增的上升趋势,铁基非晶带材压磁性能对微小应力更加敏感。
Piezomagnetic effect of Fe-based amorphous alloy ribbon was studied by applying continuous stress to Fe-based amorphous alloy ribbon and testing the nearby closed loop inductance changes.The results show that the piezomagnetic property of Fe-base amorphous alloy ribbon can be characterized by testing the nearby closed loop inductance changes of Fe-base amorphous alloy ribbon.When the frequency was equal to 1kHz,piezomag-netic property of Fe-based amorphous alloy ribbon has a good stability.And piezomagnetic property can be raised by increasing pressure.In the same pressure cases,Fe73.5 Cu1 Nb3 Si13.5 B9 alloy ribbon has a better piezo-magnetic property than that of Fe78 Si9 B13 alloy ribbon.When the frequency was equal to 100kHz,the piezomag-netic property of Fe73.5 Cu1 Nb3 Si13.5 B9 has a better stability than Fe78 Si9 B13 alloy ribbon Fe73.5 Cu1 Nb3 Si13.5 B9 al-loy ribbon show the best piezomagnetic property when the frequency was equal to 1kHz and the compressive stress was equal to 0.69MPa.When the compression stress was less than 0.1 MPa,the inductance of coil has a sharp rising trend with the increase of stress,Fe-based amorphous alloy ribbon was more sensitive to tiny stress.
参考文献
| [1] | 蒋达国,朱正吼,马广斌,夏小鸽,李塘华.FeSiB非晶薄带的压磁效应研究[J].功能材料,2007(06):911-913. |
| [2] | 黄渝鸿,吴菊英,朱正吼,付强,梅军,郭静,马广斌.基于Fe73.5Cu1Nb3Si13.5B9非晶/纳米晶粉的压磁复合材料研究[J].稀有金属,2008(02):165-170. |
| [3] | 郭沛飞,贾振元,杨兴,齐薇.压磁效应及其在传感器中的应用[J].压电与声光,2001(01):26-29. |
| [4] | 杨国宁,张万里,彭斌,蒋洪川,张文旭,易朋.非晶FeCoSiB磁弹性薄膜的应力阻抗效应[J].传感器世界,2004(11):18-21. |
| [5] | 万珍珍,朱正吼,李塘华.FeCuNbSiB/丁基橡胶复合薄膜压磁性能的研究[J].功能材料,2008(09):1494-1496. |
| [6] | 石延平.压磁式测力传感器[M].徐州:中国矿业大学出版社,2005 |
| [7] | 茅昕辉,禹金强,周勇,吴茂松,蔡炳初.FeSiB薄膜的巨磁阻抗和应力阻抗效应研究[J].真空科学与技术学报,2002(06):429-433. |
| [8] | 马广斌,朱正吼,黄渝鸿,夏小鸽,李塘华.非晶FeCuNbSiB带材压磁性能的特点[J].稀有金属材料与工程,2008(02):286-288. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%