以氯化镉和二氧化碲为原料，水合肼为还原剂和络合剂，原位制备出了纳米级混合均匀的前驱体粉末，在110~400℃氢气还原制备了碲化镉粉末，并结合X射线衍射(XRD)、热重分析(TG)、扫描电子显微镜(SEM)等分析手段研究了上述过程中物相和微观结构演变。结果表明，制备前驱体过程中四价碲被水合肼还原成纳米级的碲单质，同时镉离子以2~5μm Cd(N2 H4)x Cl2配合物的形式沉淀析出，且单质碲和Cd(N2 H4)x Cl2均匀分散；当氯化镉和二氧化碲按摩尔比1∶1进行混合时得到的前驱体经400℃氢处理后，可获得单一相组成的碲化镉粉末。
The uniformly mixing precursor powders at nanoscale size was prepared by in-situ reaction which used cadmium chloride and tellurium dioxide as raw materials,and hydrazine hydrate as a reducing agent and a com-plexing agent.The cadmium telluride was obtained by hydrogen reduction of precursor powders during 110-400℃.Moreover,the evolution of phases and microstructures were investigated by XRD,TG,SEM etc.The results show that during the preparation of precursor the tetravalent tellurium was changed to elemental telluri-um at nanoscale size,while the ions of cadmium precipitated in the form of 2-5μm Cd(N2 H4 )x Cl2 complexes. Furthermore,the elemental tellurium and Cd(N2 H4 )x Cl2 dispersed uniformly.The single phase cadmium tellu-ride can be obtained from the precursor treated by hydrogen at 400℃ and the precursor was prepared with cad-mium chloride and tellurium dioxide mixed with a molar ratio 1∶1 .
参考文献
| [1] | Irfan Irfan;Hao Lin;Wei Xia;Hsiang N. Wu;Ching W. Tang;Yongli Gao.The effect of MoO_x inter-layer on thin film CdTe/CdS solar cell[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2012:86-89. |
| [2] | 李锦,郑毓峰,徐金宝,孙严飞,陈树义.CdTe薄膜的制备方法比较及其结构性能研究[J].功能材料,2002(05):508-510. |
| [3] | 付文博,刘庭良,何绪林,张静全,冯良桓,武莉莉,李卫,黎兵,曾广根,王文武.含氯气氛退火对CdTe薄膜性质影响的交流阻抗研究[J].功能材料,2011(12):2225-2228. |
| [4] | Brooks, W.S.M.;Irvine, S.J.C.;Barrioz, V.;Clayton, A.J..Laser beam induced current measurements of Cd _(1-x)Zn _xS/CdTe solar cells[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2012:26-31. |
| [5] | C. S. Ferekides;U. Balasubramanian;R. Mamazza;V. Viswanathan;H. Zhao;D. L. Morel .CdTe thin film solar cells: device and technology issues[J].Solar Energy,2004(6):823-830. |
| [6] | Jochen Fritsche;Andreas Klein;Wolfram Jaegermonn .Thin Film Solar Cells: Materials Science at Interfaces[J].Advanced Engineering Materials,2005(10):914-920. |
| [7] | 侯仁义 .一种高纯碲化镉的制备方法[P].中国:CN101125679,2008-02-20. |
| [8] | 熊先林;刘益军;管迎博 .一种高纯碲化镉的制备方法[P].中国:CN101734630A,2010-06-16. |
| [9] | 朱世会;朱世明;朱刘 .一种碲化镉液相合成方法[P].中国:CN102086031A,2011-06-28. |
| [10] | 吴洪才 .碲化镉粉末的制备方法[P].中国:CN1380246,2002-11-20. |
| [11] | Banerjee B;Ray Chaudhuri N .Thermal studies of Cd(Ⅱ)hydrazine complexes in the solid state[J].Thermo-chimica Acta,1983,71:93-105. |
| [12] | House J E;Vandenbrook Jr Ayne J .Synthesis and ther-mal characteristics of dichlorobis(hydrazine)cadmium(Ⅱ)[J].Thermochimica Acta,1990,161:85-88. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%