采用预聚体合成法,以二羟甲基丙酸(DM-PA)和2,4-二氨基苯磺酸钠(SDBS)为亲水扩链剂,制备了一种水性聚氨酯预聚体,再将高分子乳液乙烯-醋酸乙烯酯(EVA)与去离子水均匀混合对其乳化,制得固含量高达50%磺酸型水性聚氨酯鞋用胶粘剂。利用红外光谱对 SDBS 和聚氨酯的结构进行了表征,证实了SDBS作为亲水扩链剂引入聚氨酯链上。研究了SDBS用量对胶粘剂的剥离强度、耐热性及稳定性的影响。当SDBS用量从0增加到2.5%时,皮革初期剥离力由20.98N上升至89.23N,其耐热性和稳定性也有所增强。透射电镜图片显示,与 EVA 共乳化后的磺酸型水性聚氨酯(SWPU)乳液分散均匀,呈圆球状。
Waterborne polyurethane prepolymer were synthesized by a prepolymer process using dimethylol pro-pionic acid (DMPA)and 2,4-diaminobenzenes sulfonic acid sodium salt(SDBS)as hydrophilic chain extender agent.And the sulfonic polyurethane adhesive emulsion with solid content of 50% was obtained when emulsi-fied with the mixture of ethylene-vinyl acetate copolymer(EVA)and deionized water.The structure of the film was confirmed by means of Fourier transform infrared spectroscopy (FT-IR).The results indicated that the SDBS has been successfully introduced into the polyurethane chain.The influence of the SDBS content on the primeval peel strength,heat resistance and stability of the adhesive emulsion and films were studied.The results show that when SDBS content increases from 0 to 2.5%,the primeval peel strength increases from 20.98 to 89. 23N,heat resistance and stability of the adhesive emulsion and films also increases.Transmission electron mi-croscope(TEM)photos show that SWPU emulsions emulsified with EVA dispersed well with neat appearance.
参考文献
| [1] | Lu Duanyou .Aqueous polyurethane dispersion adhesive compositions with improved heat resistance[P].US:5608000,1997-03-04. |
| [2] | Li Shaoxiong.Application of polyurethane resins[M].北京:化学工业出版社,2002:559-563. |
| [3] | 成丰,向玲,于剑昆,郑海芳,杨柳涛,罗琳,李立新.鞋用水性聚氨酯胶黏剂的制备及表征[J].高分子学报,2009(09):929-935. |
| [4] | Noble KL. .WATERBORNE POLYURETHANES[J].Progress in Organic Coatings: An International Review Journal,1997(1/4):131-136. |
| [5] | 刘若望,钟凯,袁继新,翟兰兰,张云浩.以N，N-（2-羟乙基）-2-氨基乙磺酸钠为亲水扩链剂的水性聚氨酯的制备及性能[J].材料科学与工程学报,2012(06):884-888,848. |
| [6] | Anderson J T et al.Aqueous colloidal dispersions of sul-fonated polyurethane ureas and products[P].US:6649727,2003-11-18. |
| [7] | Kukan ja D .The structure and properties of acrylic poly-urethane hybrid emulsion and comparison with physical blends[J].Journal of Applied Polymer Science,2002,78:67-80. |
| [8] | 李维盈,凌爱莲,桑鸿勋.PU乳液对VAE乳液共混改性的研究[J].化学与粘合,2002(02):49-52,55. |
| [9] | Mika Lathtinen;Rachel K Pinfield;Colin Price .The chain extension of anionic prepolymers in the preparation of aqueous poly(urethane-urea) dispersions[J].Polymer international,2003(6):1027-1034. |
| [10] | 康平平,宋文生,回金楷,陈伟,闫润娟.磺酸型水性聚氨酯分散液的合成与性能[J].涂料工业,2010(08):52-55. |
| [11] | 陈红.自乳化型聚氨酯乳液研究进展[J].粘接,1998(03):19. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%