在紫铜基体上分别制备了普通快速铜镀层和纳米Al2 O3/快速铜复合刷镀层，采用扫描电镜、金相显微镜、显微硬度计、摩擦磨损实验机对比研究了两种镀层的表面形貌、截面组织形貌、显微硬度和耐磨性。结果表明，纳米 Al2 O3颗粒的加入显著改变镀层组织形貌与性能。与普通快速铜镀层相比，纳米铜基复合刷镀层表面平整，组织更加细化致密，显微硬度增大，摩擦系数降低，减弱了磨损面的犁削效应和粘着效应，耐磨性优于普通快速铜镀层。
Traditional Cu coating and Cu/nano-Al2 O3 composite coating were prepared respectively with electro-brush plating on pure copper matrix.The surface morphology,section structure,micro-hardness and wear re-sistance of both coatings were determined and comparatively analyzed with canning electron microscope,metal-lographic microscope,digital micro-hardness tester and friction-wear tester.The results showed that,the structure,morphology and properties of Cu/nano-Al2 O3 composite coating are changed due to adding nano-Al2 O3 particles to the Cu based coating.The surface morphology of Cu/nano-Al2 O3 composite coating was more leveling and smooth,the microstructure was more compact,micro-hardness was higher and friction coefficient was lower than that of traditional Cu coating.Cu/nano-Al2 O3 coating has strong resistance effects on plough and adhesion wear.The wear resistance of Cu/nano-Al2 O3 composite coating was superior to that of traditional Cu coating.
参考文献
| [1] | 张永忠,金具涛,涂义,石力开.纯铜表面激光熔覆铜合金涂层的组织及耐磨性[J].金属热处理,2009(04):28-32. |
| [2] | 徐滨士.纳米表面工程[M].北京:化学工业出版社,2004 |
| [3] | 宾胜武.刷镀技术[M].北京:化学工业出版社,1996:1-37. |
| [4] | Spanoua S;Pavlatou E A;Spyrellis N .Ni/nano-TiO2 com-posite electrodeposits:textural and structural modifica-tions[J].Electrochimica Acta,2009,254:2547-2555. |
| [5] | 周仕勇;沈承金;史 强 等.纳米 TiO2-Ni 基镀层的电刷 镀沉积行为研究[J].功能材料,2011,42:251-254. |
| [6] | 李颖,赵盟月,董企铭,邹文俊,胡余沛.纳米金刚石/镍复合电刷镀层的显微结构研究[J].功能材料,2010(09):1588-1591. |
| [7] | 高加强,刘磊,沈彬,朱建华,胡文彬,文江.纳米Al2O3粒子增强化学镀Ni-P复合镀层的组织结构[J].上海交通大学学报,2005(02):265-269. |
| [8] | 周广宏,丁红燕,章跃.Ni-P-Nano-Al2O3化学复合镀层的磨损机理[J].金属热处理,2004(07):38-40. |
| [9] | 周广宏,丁红燕.非晶态Ni-P合金与纳米Al2O3微粒复合镀层的制备[J].材料热处理学报,2004(04):81-84. |
| [10] | Alirezaei S;Monirvaghefi SM;Salehi M;Saatchi A .Effect of alumina content on surface morphology and hardness of Ni-P-Al2O3(alpha) electroless composite coatings[J].Surface & Coatings Technology,2004(2/3):170-175. |
| [11] | 杜锋,江中浩,刘先黎.电刷镀纳米镍薄膜表面形貌和沉积生长机理分析[J].长春工业大学学报（自然科学版）,2007(01):5-8. |
| [12] | 赵 盟;李 颖;位 星 等.Nano-diamond/Ni 复合电刷镀层的组织形貌的研究[J].金刚石与磨料模具工程,2010,30(176):63-66. |
| [13] | 徐伟毅;徐滨士;蒋 斌.Al2 O3-Ni 电刷镀复合镀层组织与沉积机理[J].材料工程,2003(07):31-35. |
| [14] | 侯峰岩,王为,刘家臣,郭鹤桐.ZrO2纳米颗粒在Ni-ZrO2复合镀层中的分散性对镀层结构及性能的影响[J].材料工程,2004(03):21-23,27. |
| [15] | 吴化,陈涛,王庆辉.电沉积Ni-SiC纳米复合镀层的显微组织分析[J].材料工程,2011(12):48-52. |
| [16] | 陈海涛;李忠盛;孙彩云 等.Al2 O3/Ni-Cr-Cr3 C2 耐磨复合涂层制备及其摩擦学特性研究[J].稀有金属材料与工程,2011,40(02):447-451. |
| [17] | 方佳,刘炳,代廷海,贾伯早,李振华,郭莉燕.Al2O3颗粒增强铝锰合金复合材料性能研究[J].铸造技术,2011(09):1305-1308. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%