内养护(internal curing)是抑制高强混凝土自收缩研究的热点。研究了新型内养护材料对高强混凝土自收缩的影响规律，通过孔结构分析了内养护作用机理。结果表明，内养护材料用量20~25 kg/m3、粒径<100μm时，抑制自收缩效果较佳。当混凝土中有锰渣微粉和粉煤灰时，内养护材料(internal curing agents)可与之发挥协同抑制效应。压汞分析证实，内养护减少了混凝土中对收缩不利的9~50 nm 毛细孔数量，增加了9 nm以下凝胶孔数量。
Internal curing has become a hot topic in mitigating autogenous shrinkage of high strength concrete, HSC.In this thesis,relationship between autogenous shrinkage and new internal curing materials was carried out and internal curing mechanism was further investigated.The results show ICA that provides useful refer-ence for solving early-age shrinkage.When the amount of ICA 20 to 25 kg/m3 ,the particle diameter below 100μm,autogenous shrinkage of HSC was well mitigated.When manganese slag powder and fly ash in concrete, its can play an assembling role on internal curing as ICA.MIP analysis confirmed that mitigation of autogenous shrinkage lies in reducing the amount of shrinkage adversely 9-50 nm capillary pores,and increasing the number of below 9 nm gel pores by internal curing.
参考文献
| [1] | Konstantin Kovler;David A. Lange;Henrik Stang .Early age concrete--properties and performance[J].Cement & concrete composites,2004(5):413-415. |
| [2] | 李悦,谈慕华,张雄,吴科如.混凝土的自收缩及其研究进展[J].建筑材料学报,2000(03):252-257. |
| [3] | 陈德鹏,钱春香,高桂波,赵洪凯.高吸水树脂对混凝土收缩开裂的改善作用及其机理[J].功能材料,2007(03):475-478. |
| [4] | Wang Fazhou;Zhou Yufei;Peng Bo et al.Autogenous shrinkage of concrete with super-aborbent polymer[J].ACI Material Journal,2009,106(2):123-127. |
| [5] | Persson B .Self-desiccation and its importance in concrete technology[J].Materials and Structures,1997,30(5):293-305. |
| [6] | Piérard Jean;Pollet V;Cauberg N.Mitigating autoge-nous shrinkage in HPC by internal curing using superab-sorbent polymers[A].Bagneux,2006:97-106. |
| [7] | A?tcin P C;徐志惠;刘数华.高性能混凝土耐久性综述[J].商品混凝土,2011(02):33-38. |
| [8] | Hoff G C .The use of lightweight fines for the internal curing of concrete[R].Lake Bluff:Northeast Solite Cor-poration,2004. |
| [9] | Lura Pietro;Durand Felix;Jensen Ole Mejlhede.Autog-enous strain of cement pastes with superabsorbent poly-mers[A].Lyngby,2006:57-65. |
| [10] | 蒋正武,孙振平,王培铭,王新友.高性能混凝土中自干燥效应的研究[J].建筑材料学报,2004(01):19-24. |
| [11] | LIU Rong-jin,DING Qing-jun,CHEN Ping,YANG Guang-yao.Durability of Concrete Made with Manganese Slag as Supplementary Cementitious Materials[J].上海交通大学学报（英文版）,2012(03):345-349. |
| [12] | 刘荣进,陈平.水淬锰渣的成分、结构及性能研究[J].铁合金,2009(03):42-46. |
| [13] | 杨玉红,李悦,杜修力.自密实混凝土早期自收缩及微观孔结构研究[J].建筑材料学报,2010(05):601-606. |
| [14] | 马丽媛 .高强混凝土收缩开裂的研究[D].中国建筑材料科学研究院,2001. |
| [15] | 王信刚 .外加剂对水泥基材料早期变形性能影响的研究[D].武汉大学,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%