采用光学显微镜、扫描电镜、硬度试验机和电子万用试验机等研究了合金的显微组织、晶间腐蚀情况和力学性能.结果表明,经过稳定化处理后的试样析出了不连续的第二相,稳定化处理和冷轧后的试样均无晶间腐蚀现象,试样在180℃下退火后,试样内形成了等轴晶粒,晶界上连续分布的β相,出现了晶间腐蚀现象,保温90h比15h晶界上析出β相更多,试样的晶间腐蚀更加明显；合金稳定化处理后硬度最高,冷轧后试样的硬度最低,在180℃下退火保温15和90h的硬度比冷轧后高,但低于稳定化处理后的试样,稳定化处理和退火后的试样的塑性较冷轧态好.
参考文献
| [1] | Tamara Radetic;Miljana Popovic;Endre Romhanji.Microstructure evolution of a modified AA5083 aluminum alloy during a multistage homogenization treatment[J].Materials Characterization,2012:16-27. |
| [2] | Jafarzadeh K;Shahrabi T;Hadavi S M M et al.Role of chloride ion and dissolved oxygen in electrochemical corrosi on of AA 5083-H321 aluminum-magnesium alloy in NaCl solutions under flow conditions[J].Journal of Materials Science and Technology,2007,23:623-628. |
| [3] | Zhalehfar F;Hosseinipour S J;Nourouzi S.Numerical investigation into the effect of uniaxial and biaxial pre strain on forming limit diagram of 5083 aluminum alloy[A].Seoul,Korea,2011:165-172. |
| [4] | 温庆红.5083/5086合金板材晶间腐蚀特征图谱研究[J].铝加工,2009(05):32-36. |
| [5] | 罗兵辉,单毅敏,柏振海.退火温度对淬火后冷轧5083铝合金组织及腐蚀性能的影响[J].中南大学学报（自然科学版）,2007(05):802-808. |
| [6] | 郜余军,马立群,丁毅,赵相玉,杨猛,曹歆昕,瞿鑫鑫.导电剂对储氢合金MLNi3.8Co0.75Mn0.4Al0.2电极电化学性能的影响[J].有色金属,2011(02):38-41. |
| [7] | 张雅玲.稳定化处理对5083合金冷轧板组织和性能的影响[J].轻合金加工技术,2008(03):22-23,53. |
| [8] | 陈惠芬.金属学与热处理[M].北京:冶金工业出版社,1999:25-27. |
| [9] | 刘继华,李荻,刘培英.热处理对7075铝合金应力腐蚀及断口形貌的影响[J].材料热处理学报,2010(07):109-113. |
| [10] | 郝勇,史庆南,陈家欣.退火温度对7005铝合金力学性能与显微组织的影响[J].热加工工艺,2011(10):173-175,203. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%