以玉米淀粉和聚乳酸为原料，甘油为增塑剂，利用熔融挤出法制备了淀粉/聚乳酸复合材料。研究了甘油用量对复合材料熔融流动性、界面相容性、力学性能、吸水率以及流变性能的影响。结果表明，甘油用量增加可以提高复合材料的熔融流动性能，降低复数粘度，有利于提高复合材料的加工性能。甘油的加入提高了淀粉和聚乳酸的界面相容性，并且甘油用量增加，相容性提高越多。相容性提高使复合材料的拉伸强度提高。增塑剂能够破坏淀粉的结晶结构，降低分子间相互作用力，提高复合材料的柔顺性。随着甘油用量增加，淀粉/聚乳酸复合材料的弯曲强度降低，储能模量也逐渐降低，但断裂伸长率增大。吸水率测试结果表明，甘油用量增加有利于提高复合材料的耐水性能。
Starch/polylactic acid composites were prepared by melt extrusion method with corn starch and poly-lactic acid as raw material,glycerol as the plasticizer.Melt fluidity,interfacial compatibility,mechanical prop-erties,water absorption rate and rheological properties of composite was studied by glycerol content.The re-sults show that the increased glycerol content was increased melt flow properties of composite materials,and reduce the complex viscosity,which helps to improve the processing performance of the composite material. The addition of glycerol increased the interface compatibility between starch and polylactic acid,and with glyc-erol content increased,the compatibility was improved more.Compatibility improve was increased the tensile strength of the composite.Plasticizer can damage the crystalline structure of starch,reduce the interaction of molecules,and so increase flexibility of composite material.Thus,with glycerol dosage increase,the bending strength and storage modulus were decreased,but the elongation at break increased.Water absorption test re-sults show that increased glycerol dosage was help to improve the water resistance of composite materials.
参考文献
| [1] | 窦庶华,孙姣霞,阮长顺,张晓彦,吴进川,王远亮.新型聚乳酸-聚酰亚胺嵌段共聚物的合成与表征[J].功能材料,2012(03):317-319,323. |
| [2] | Hua Wang;Xiuzhi Sun;Paul Seib .Strengthening Blends of Poly(lactic acid) and Starch with Methylenediphenyl Diisocyanate[J].Journal of Applied Polymer Science,2001(7):1761-1767. |
| [3] | 左迎峰,顾继友,谭海彦,张彦华.复合增塑剂种类对玉米淀粉塑化性能的影响[J].功能材料,2013(09):1365-1368. |
| [4] | 曲敏杰,李晶,马春,崔佳.聚乳酸/淀粉共混复合材料研究进展[J].塑料科技,2008(07):74-80. |
| [5] | 吴学森,王伟.甘油对聚乳酸/淀粉复合材料机械性能的影响[J].化工时刊,2009(01):1-4. |
| [6] | Maiti S N;Hassan M R .Melt theological properties of PP-wood flour composites[J].Journal of Applied poly-mer Science,1989,37(07):2019-2032. |
| [7] | JUN WUK PARK;SEUNG SOON IM;SOO HYUN KIM;YOUNG HA KIM .Biodegradable Polymer Blends of Poly(L-lactic acid) and Gelatinized Starch[J].Polymer engineering and science,2000(12):2539-2550. |
| [8] | 由英才,朱常英,焦京亮,沈忻.淀粉/DL-丙交酯接枝共聚物的合成和生物降解性能研究[J].高分子学报,2000(06):746-750. |
| [9] | 张清松,邓晶晶,贺湘伟,吴智华.增塑剂对聚乳酸/热塑性淀粉共混物结构与性能的影响[J].塑料工业,2009(11):51-54. |
| [10] | 钱欣,沈兆宏,潘柯良.增塑剂对聚乳酸性能的影响[J].塑料工业,2006(12):63-65. |
| [11] | 徐配弦.高聚物流变学及其应用[M].北京:化学工业出版社,2003:8-11. |
| [12] | Cassagnau P.;Melis F. .Non-linear viscoelastic behaviour and modulus recovery in silica filled polymers[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(21):6607-6615. |
| [13] | 高华 .木粉/马来酸酐接枝聚烯烃共混物复合材料[D].哈尔滨:东北林业大学,2011. |
| [14] | 张水洞,黄汉雄,颜斌玉,蒋果.醋酸淀粉/聚乳酸的制备及性能的影响研究[J].化学研究与应用,2010(03):387-391. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%