先对碳纤维进行 HCl 预处理,然后通过溶胶-凝胶技术在预处理后碳纤维表面涂覆 HA 涂层,最后利用离心成型技术制备改性碳纤维增强 HA复合材料.重点研究碳纤维的改性工艺,观察改性前后碳纤维表面的微观形貌,分析 HA 浆料固相含量对离心过程中物质分离现象的影响,测量不同碳纤维含量下烧结产物的抗弯强度和断裂韧度.研究结果表明,经过HCl和提拉HA溶胶复合处理的碳纤维表面具有1层致密的、与基体结合性能较好的膜层.固相含量为50％(质量分数)HA 浆料在2860 g 加速度下离心后所得生坯密度均匀,SEM观察表明烧结产物致密,没有明显的物质分离现象.当碳纤维含量为2％(质量分数)时,离心成型制备的改性碳纤维/HA 复合材料的抗弯强度达到最大值93．5 MPa；当碳纤维含量为2．5％(质量分数)时,该复合材料的断裂韧度达到最大值1．96 MPa?m1/2.
The carbon fibers treated by HCl were coated with HA layers using sol-gel technology and then used to fabricate the treated C-fibers reinforced HA composites by centrifugal slip casting technology.The treated technologies of C-fibers were studied,micro-morphologies of the untreated and treated C-fibers were observed, the effect of the solid content of HA slurries on mass segregation during centrifugal process was analyzed,and mechanical properties of sintered composites were measured.The results show the carbon fibers after HCl dis-posal and dip in HA sol have a compact layer which has better contact with HA matrix.After centrifuged at 2 860 g acceleration,the green compacts have uniform density.SEM observation shows the sintered composites have compact microstructure and no obvious mass segregation phenomenon.The treated CF/HA composites prepared by centrifugal slip casting have the highest bending strength of 93.5 MPa and flexural toughness of 1.96 MPa?m1/2 ,respectively,when the contents of C-fibers was 2% and 2.5wt%.
参考文献
| [1] | 赵冰,杜荣归,林昌健.羟基磷灰石生物陶瓷材料的制备及其新进展[J].功能材料,2003(02):126-129,132. |
| [2] | 宋江凤,刘咏,张莹.水热法合成不同形貌羟基磷灰石[J].粉末冶金材料科学与工程,2010(05):505-510. |
| [3] | Zafer Evis;Metin Usta;Isil Kutbay .Improvement in sinterability and phase stability of hydroxyapatite and partially stabilized zirconia composites[J].Journal of the European Ceramic Society,2009(4):621-628. |
| [4] | 曾丽平,曹丽云,黄剑锋,郭申.HA改性短切碳纤维/PMMA生物复合材料力学性能的研究[J].无机材料学报,2009(03):475-479. |
| [5] | 赵俊亮,付涛,憨勇,徐可为.碳纤维增强羟基磷灰石/环氧树脂复合材料的制备与力学性能[J].材料科学与工程学报,2003(05):640-643. |
| [6] | Rei sel A D;Berroth K;Neubauer R.Unreinforced and carbon fiber reinforced hydroxyapatite:resistance against microabrasion[J].Journal of the European Ce-ramic Society,2004(24):2131-2139. |
| [7] | Biesheuvel P B;Verweij H .Calculation of the composi-tion profile of a functionally graded materials produced by centrifugal casting[J].Journal of the American Ceramic Society,2000,83(04):743-749. |
| [8] | 于景媛,李强,李晓东,孙旭东.离心成型结合模板法制备孔径均匀的多孔氧化铝陶瓷[J].功能材料,2007(03):397-399,403. |
| [9] | 宋贤良,陈玲,叶建东,温其标.不同颗粒尺寸α-Al2O3粉体制备稳定浆料的研究[J].硅酸盐学报,2003(07):702-706. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%