将普通零价锌在滚压振动磨中研磨13 h后,制备出不规则片状、粒径为20~30 nm的纳米零价锌(NZVZ)。采用所制备的 NZVZ 降解甲基橙,系统研究了搅拌速度、NZVZ 投入量、甲基橙初始浓度和NaCl的加入对甲基橙降解效率的影响。结果表明, NZVZ表面反应活性增高,反应60 min 时,2 g/L 的NZVZ对甲基橙降解率为98.5%,比4 g/L 的普通零价锌高60.3%,其中间降解产物有对氨基苯磺酸和对氨基二甲基苯胺。降解率随转速、NZVZ 投入量的增加而升高,随 MO 初始浓度的增加而降低；加入 NaCl能促进反应进行,且随着投入量增加降解率增加。通过对实验数据的分析,验证 NZVZ降解 MO 过程符合伪一级动力学方程式。
The ordinary zinc powder was milled for 1 3 h with roller vibration milling and produced irregular sheet nanoscale zero-valent zinc particles(NZVZ).The particle size was between 20 and 30 nm.This paper here was focused on the degradation of water soluble methyl orange(MO)by NZVZ,and rotation speed of magnetic stirrer,NZVZ dosage,initial MO concentration and NaCl dosage were studied systematically.It was found that the degradation of MO with 2 g/L of NZVZ was 98.5% in 60 min,which was 60.3% higher than that of using 4 g/L of ordinary zinc powder,the sulfanilic acid and 1 ,4-benzenediamine,N,N-dimethyl-as degradation pro-gress products were identified.Degradation was enhanced with increase of rotation speed and NZVZ dosage, while decreased with increase of initial MO concentration.Moreover,the existence of NaCl can promote the re-action procress and degradation increased with increase of NaCl dosage.Kinetic analyses based on the experi-mental data elucidated that the degradation process followed the pseudo first-order kinetic equation.
参考文献
| [1] | Wang Xiaorong;Wu Pingxiao;Zhang Xing et al.Study on the performance of photocatalytic degradation of methyl-ene blue using ZnAlTi layered double hydroxides[J].Journal of Functional Materials,2012,43(20):2799-2083. |
| [2] | 胡婷婷 .高铁酸钾降解偶氮类染料研究[D].同济大学,2008. |
| [3] | ABINASH AGRAWAL;PAUL G. TRATNYEK .Reduction of Nitro Aromatic Compounds by Zero-Valent Iron Metal[J].Environmental Science & Technology: ES&T,1996(1):153-160. |
| [4] | Shu-Hong Li;Yue Zhao;Jian Chu;Wen-Wei Li;Han-Qing Yu;Gang Liu.Electrochemical degradation of methyl orange on Pt-Bi/C nanostructured electrode by a square-wave potential method[J].Electrochimica Acta,2013:93-101. |
| [5] | 刘士姮,汪世龙,孙晓宇,李文哲,倪亚明,王文峰,王敏,姚思德.脉冲辐解技术研究偶氮染料甲基橙水相降解的微观机理[J].化学学报,2004(08):818-822. |
| [6] | Matheson L J;Tratnyek P G .Reductive dehalogenation of chlorinated methanes by iron metal[J].Environmental Science and Technology,1994,28(12):2045-2053. |
| [7] | Zhang, Xianlan;Deng, Baolin;Guo, Jing;Wang, Yang;Lan, Yeqing .Ligand-assisted degradation of carbon tetrachloride by microscale zero-valent iron[J].Journal of Environmental Management,2011(4):1328-1333. |
| [8] | Hozalski R M;Zhang L;Arnold W A .Reduction of haloace-tic acids by Fe0:implications for treatment and fate[J].En-viron Sci Technol,2001,35(11):2258-2263. |
| [9] | Paul Westerhoff;Jennifer James .Nitrate removal in zero-valent iron packed columns[J].Water research: A journal of the international water association,2003(8):1818-1830. |
| [10] | Zhen Zhang;Zhiwei Hao;Yueping Yang .Reductive denitrification kinetics of nitrite by zero-valent iron[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2010(1/3):158-162. |
| [11] | Chen SY;Chen WH;Shih CJ .Heavy metal removal from wastewater using zero-valent iron nanoparticles[J].Water Science and Technology,2008(10):1947-1954. |
| [12] | Ying Han;Zhong-lin Chen;Li-na Tong;Lei Yang;Ji-min Shen;Bin-yuan Wang;Yue Liu;Yu Liu;Qian Chen .Reduction of N-Nitrosodimethylamine with zero-valent zinc[J].Water research: A journal of the international water association,2013(1):216-224. |
| [13] | Sayles G D;You G;Wang M et al.DDT,DDD,and DDE dechlorination by zero-valent iron[J].Environmental Science and Technology,1997,31(12):3448-3454. |
| [14] | SANGKIL NAM;PAUL G. TRATNYEK .REDUCTION OF AZO DYES WITH ZERO-VALENT IRON[J].Water research: A journal of the international water association,2000(6):1837-1845. |
| [15] | Wu Deli;Ma Luming.Research progress of pollutants degradation by zero valent metals and their compounds[J].Environmental Science Trends,2005(02):32-35. |
| [16] | Jing Guo;Danjun Jiang;Yong Wu;Pei Zhou;Yeqing Lan.Degradation of methyl orange by Zn(0) assisted with silica gel[J].Journal of hazardous materials,2011:290-296. |
| [17] | Tratnyek P G;Salter A J;Nurmi J T et al.Environ-mental applications of zerovalent metals:iron vs.zinc[J].Nanoscale Mater Chem Environ Appl,2010,1045:165-178. |
| [18] | Nurmi JT;Tratnyek PG;Sarathy V;Baer DR;Amonette JE;Pecher K;Wang CM;Linehan JC;Matson DW;Penn RL .Characterization and properties of metallic iron nanoparticles: Spectroscopy, electrochemistry, and kinetics[J].Environmental Science & Technology: ES&T,2005(5):1221-1230. |
| [19] | T. Satapanajaru;C. Chompuchan;P. Suntomchot .Enhancing decolorization of Reactive Black 5 and Reactive Red 198 during nano zerovalent iron treatment[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2011(1/3):218-230. |
| [20] | Jing Fan;Yanhui Guo;Jianji Wang;Maohong Fan .Rapid decolorization of azo dye methyl orange in aqueous solution by nanoscale zerovalent iron particles[J].Journal of hazardous materials,2009(2/3):904-910. |
| [21] | 王树林.振动超微颗粒制备技术的新进展[J].中国粉体技术,2001(05):42-46. |
| [22] | 徐波,王树林,李生娟,韩光强,陈星建,丁浩冉.纳米锌水解制氢实验[J].化工学报,2009(05):1275-1280. |
| [23] | 吴明霞,王树林,丁浩冉,韩光强.水解锌纳米结构对甲基橙的光催化降解[J].化工学报,2008(04):1016-1021. |
| [24] | Ball P;Garwin L .Science at the atomic scale[J].Na-ture,1992,355(6363):761-766. |
| [25] | Malyala R V;Chaudhari R V .Hydrogenation of 2,4-di-nitrotoluene using a supported Ni catalyst:reaction ki-netics and semibatchslurryreactor modeling[J].Industrial and Engineering Chemistry Research,1999,38:2906-2915. |
| [26] | 李贵贤,司海娟,马建军,杨磊,王晓宁,范宗良.2,4-二硝基甲苯加氢反应历程及操作条件对反应速率的影响[J].兰州理工大学学报,2008(03):60-64. |
| [27] | Rafael Hernandez;Mark Zappi;Chiang-HaiKuo .Chloride Effect on TNT Degradation by Zerovalent Iron or Zinc during Water Treatment[J].Environmental Science & Technology: ES&T,2004(19):5157-5163. |
| [28] | Upadhyay S K.Chemical kinetics and reaction dynamics[M].New York:Springer-Verlag,2006:20-25. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%