通过以肉豆蔻酸-乙醇为疏水剂，采用简单一步法在金属铜表面上构筑超疏水薄膜，经过扫描电子显微镜(SEM)、接触角测量仪和防垢性能测试技术分析，结果表明，铜试样表面形成树枝状的肉豆蔻酸盐微簇，接触角达到了160°，并且具有较好的抗结垢性能；肉豆蔻酸-乙醇溶液的浓度、浸泡时间、浸泡温度对构筑铜试样表面的超疏水性起着关键性的影响。研究结果有利于更好地理解肉豆蔻酸铜表面超疏水性复合材料的形成机理，对有色金属超疏水材料的制备提供新的设计思路。
We construct super hydrophobic films on the surface of metallic copper by simple one-step method. The technical analysis includes scanning of electron microscope,contact angle measurement and antifouling per-formance test.The result shows that dendritic myristic acid micro-clusters were formed on the surface of copper specimen.The contact angle reached 160°and the antifouling performance was nice.Three elements played a key role in constructing hydrophobicity on the surface of copper specimen.The three elements were the concentra-tion of ethanol solution with myristic acid,soaking time and soaking temperature.These results aid ourunder-standing of the formation of superhydrophobic myristic acid copper composites,and the design of superhydro-phobic of non-ferrous metals materials.
参考文献
| [1] | Onda T;Shibuichi S;Satoh N et al.Super-water-repel-lent fractal surfaces[J].LANGMUIR,1996,12(09):2125-2127. |
| [2] | Venkatasubramanian, R.;Jin, K.;Pesika, N.S. .Use of electrochemical deposition to create randomly rough surfaces and roughness gradients[J].Langmuir: The ACS Journal of Surfaces and Colloids,2011(7):3261-3265. |
| [3] | Zhang Xi;Shi Feng;Niu Jia et al.Superhydrophobic surface:from structural control to functional application[J].Journal of Materials Chemistry,2008,18:621-633. |
| [4] | Paul E. Hintze;Luz Marina Calle .Electrochemical properties and corrosion protection of organosilane self-assembled monolayers on aluminum 2024-T3[J].Electrochimica Acta,2006(8/9):1761-1766. |
| [5] | Patankar NA .Mimicking the lotus effect: Influence of double roughness structures and slender pillars[J].Langmuir: The ACS Journal of Surfaces and Colloids,2004(19):8209-8213. |
| [6] | 宋根萍,夏冬祥.一步法合成聚苯胺/十二烷基苯磺酸钠超疏水复合材料[J].物理化学学报,2014(03):583-588. |
| [7] | 葛圣松,李娟,邵谦,刘青云.钢铁表面超疏水膜的制备与表征[J].功能材料,2012(05):645-649. |
| [8] | Hiroshi Yabu;Masatsugu Shimomura .Single-Step Fabrication of Transparent Superhydrophobic Porous Polymer Films[J].Chemistry of Materials,2005(21):5231-5234. |
| [9] | Lin Feng;Zhongyi Zhang;Zhenhong Mai;Yongmei Ma;Biqian Liu;Lei Jiang;Daoben Zhu .A Super-Hydrophobic and Super-Oleophilic Coating Mesh Film for the Separation of Oil and Water[J].Angewandte Chemie,2004(15):2012-2014. |
| [10] | Khorasani MT;Mirzadeh H;Kermani Z .Wettability of porous polydimethylsiloxane surface: morphology study[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(3/4):339-345. |
| [11] | Zhu Liang;Feng Yanying;Ye Xiongying et al.Tuning wettablity and getting superhydrophobic surface by con-trolling surface roughness with well-designed micro-structures[J].Sensors and Actuators A-physical,2006,130-131:595-600. |
| [12] | Allara D L;Nuzzo R G .Quantitative infrared spectro-scopic determination of equilibrium structures of solu-tion-adsorbed n-alkanoic acids on an oxidized aluminum surface[J].LANGMUIR,1985,1(01):52-60. |
| [13] | Jiang Lei;Feng Lin.Bio-mimic intelligent nano-interfa-cial materials[M].北京:化学工业出版社,2007 |
| [14] | Xia Fan;Jiang Lei .Bio-inspired,smart,multiscale in-terfacial material[J].Advanced Materials,2008,20:2842-2858. |
| [15] | Wang Shutao .Fabrication and characterization of bio-mimic smart nano interface with special wettability[D].Beijing:Institute of Chemistry Chinese Academy of Sci-ences,2005. |
| [16] | Wang Shutao;Feng Lin;Jiang Lei .One-step solution-immersion process for the fabrication of stable bionic su-perhydrophobic surfaces[J].Advanced Mater,2006,18:767-770. |
| [17] | 刘通,刘涛,陈守刚,程莎,尹衍升.超疏水表面改善铝基材料的抗海水腐蚀性能[J].无机化学学报,2008(11):1859-1863. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%