研究首先制得二元脂肪酸低共熔物,然后将用静电纺丝法制备不同Si O 2含量的、并对其进行炭化的PAN/SiO2纳米纤维膜作为支撑材料,吸附二元脂肪酸低共熔物制得碳/Si O 2纳米纤维膜基定形相变材料(CSNPCM),利用扫描电子显微镜(SEM)、差示扫描量热仪(DSC)等对制备出的定形相变材料的形貌结构和储热性能进行分析和表征。随着 Si O 2含量的增加,定形相变材料对二元脂肪酸低共熔物的吸附容量有所降低。SEM结果表明,二元脂肪酸低共熔物均匀地包埋、分散在多孔纳米纤维膜的三维网络结构中。DSC测试结果表明,SiO2的加入降低了定形相变材料的相变潜热,对其相变温度无太大影响。
Firstly,binary fatty acid eutectics were prepared by melt blending and ultrasonic dispersion technique in this research,then the PAN/SiO2 nanofibrous mats with different content of SiO2 prepared by using electro-spinning method,which after carbonization were taken as supporting materials.The form-stable phase change materials based on C/SiO2 nanofibrous mats (CSNPCM)were fabricated by adsorbing binary fatty acid eutec-tics.The structural morphologies and thermal energy storage properties of form-stable phase change materials were characterized by scanning electron microscope (SEM)and differential scanning calorimeter (DSC),respec-tively.With the increase of SiO2 ,the adsorption capacity of binary fatty acid eutectics in turn reduce.SEM re-sults show that binary fatty acid eutectics embeded and dispersed evenly in the three dimensional network struc-ture of porous nanofibrous mats.DSC results show that the addition of SiO2 decrease the phase change latent heat of form-stable phase change materials,whereas there are no appreciable changes on the phase transition temperatures.
参考文献
| [1] | 郭静,相恒学,徐德增,王倩倩.硬脂酸-月桂酸二元复合相变材料[J].大连工业大学学报,2012(01):60-63. |
| [2] | Yang Ying;Sun Yanli;Kan Kan et al.Preparation and shape control of SiO2 nanofiber by electrospining[J].Journal of Functional Materials,2013,44(01):36-38. |
| [3] | Li Min;Wu Zhishen;Kao Hongtao et al.Experimental in-vestigation of preparation and thermal performances of paraf-fin/bentonite composite phase change material[J].Energy Conversion & Management,2011,52(11):3275-3281. |
| [4] | Feng, L.;Zheng, J.;Yang, H.;Guo, Y.;Li, W.;Li, X. .Preparation and characterization of polyethylene glycol/active carbon composites as shape-stabilized phase change materials[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2011(2):644-650. |
| [5] | San A .Form-stable paraffin/high density polyethylene composites as solid-liquid phase change material for ther-mal energy storage:Preparation and thermal properties[J].Energy Conversion & Management,2004,45(13-14):2033-2042. |
| [6] | Cecilia Castellon .Effect of microencapsulated phase change material in sandwich panels[J].Renewable energy,2010(10):2370. |
| [7] | 刘太奇,刘瑞雪,孙雁男,赵小龙.静电纺聚乙烯醇/纳米二氧化钛超细纤维的水稳定性[J].高分子材料科学与工程,2013(12):98-102. |
| [8] | 罗红军,黄勇.PAN/PEO和CA/PEO同轴静电纺丝纤维的制备及其力学性能研究[J].高分子通报,2013(06):64-70. |
| [9] | 柯惠珍,蔡以兵,魏取福,乔辉.纳米SiO_2对静电纺LA-PA/PET复合相变纤维形态和热学性能的影响[J].功能材料,2012(03):309-312. |
| [10] | Fang, G.;Li, H.;Chen, Z.;Liu, X. .Preparation and properties of palmitic acid/SiO2 composites with flame retardant as thermal energy storage materials[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2011(7):1875-1881. |
| [11] | Lv Shilei;Zhu Neng;Feng Guohui .Eutectic mixtures of capric acid and lauric acid applied in building wallboards for heat energy storage[J].Energy and buildings,2006(6):708-711. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%