为研究LVL木纤维复合材在高温中和高温后的抗弯性能，对104个试样进行了温度在20~225℃下的三点静态抗弯测试。研究结果表明，随着温度的升高，高温中和高温后的抗弯强度、抗弯弹性模量、延性系数均明显减小；相对于高温中的试样，高温后的抗弯强度和抗弯弹性模量均明显较高，而延性系数则较低。根据回归分析，提出了LVL在高温中和高温后的抗弯强度与温度的关系模型，该模型预测结果与实测值吻合良好。
Static 3-point bending tests,with a total of 104 specimens,were carried out to study the bending prop-erties of LVL wood composite at and after exposure to high temperature in the range from 20 to 225 ℃.The test results show that the bending strength (MOR),modulus of elasticity (MOE)and ductility coefficient (μ) of LVL wood composite at and after exposure to high temperature decrease with the increase of the temperature. However,except for theμ,both the MOR and MOE of LVL wood composite at exposure to high temperature are lower than that after exposure to high temperature.A statistical regression-based model,as a function of thermal exposure temperature,was developed and evaluated for predicted the strength loss of LVL wood com-posite.The predicted theoretical results were consistent with the observed values.
参考文献
| [1] | 潘景龙;祝恩淳.木结构设计原理[M].北京:中国建筑工业出版社,2009:70-79. |
| [2] | GB 50005-2003.木结构设计规范[S]. |
| [3] | Zhou Jianhui;Hu Chuanshuang;Hu Shuofei et al.Effects of temperature on the bending performance of wood-based panels[J].Bioresources,2012,7(03):3597-3606. |
| [4] | Moraes P D;Rogaume Y;Bocquet J F .Influence of the temperature on the embedding strength[J].Holz Roh-Werkst,2005,63(04):297-302. |
| [5] | Schaffer E L .Effect of pyrolytic temperature on the longi-tudinal strength of dry douglas fir[J].J Test Eval,1973,1(04):319-329. |
| [6] | Arijit Sinha;John A. Nairn;Rakesh Gupta .Thermal degradation of bending strength of plywood and oriented strand board: a kinetics approach[J].Wood science and technology,2011(2):315-330. |
| [7] | Arijit Sinha;Rakesh Gupta;John A. Nairn .Thermal degradation of bending properties of structural wood and wood-based composites[J].Holzforschung,2011(2):221-229. |
| [8] | 张盛东,黄承辉,刘静.燃烧后木材顺纹抗压性能试验研究[J].建筑材料学报,2013(04):730-733,738. |
| [9] | 刘其梅;彭万喜;张党权 等.热处理对刨花板力学性质的影响[J].功能材料,2007,38(S):3482-3484. |
| [10] | Standard test methods for small clear specimens of timber,American society for testing and materials[S].PA:West Conshohocken |
| [11] | Chopra A K.Dynamics of structures:theory and appli-cations to earthquake engineering[M].Beij ing:Tsing-hua University Press,2009:264-265. |
| [12] | Beall F C;Eickner H W .Thermal degradation of wood component.Forest products research paper[R].FPL 130,1970. |
| [13] | 杜强;贾丽艳.SPSS 统计分析[M].北京:人民邮电出版社,2012:201-205. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%