采用数显显微硬度计、扫描电子显微镜、X射线衍射仪、压汞仪和固体核磁共振波谱仪分析了混凝土材料的细观实验力学性能、微观形貌、化学组成和孔隙结构。结果表明：海水侵蚀环境下，混凝土界面区附近聚集石膏、钙矾石等晶体，导致溶出性或膨胀性破坏；通过掺入矿粉，细化混凝土的孔隙、改善界面区的力学性能，但矿粉掺量超过30％后的孔隙细化效果不佳，且使孔径分布呈两极化趋势，无害孔和多害孔明显增加，少害孔和有害孔急剧减少；核磁共振波谱仪分析表明其胶凝体系中29 Si 所对应的共振频率降低，化学位移向负值方向移动，凝胶产物中的硅氧四面体除以Q1、Q2和 Q2(1Al)形式存在，还以 Q3和 Q4形式存在。
The evolution of microstructure of concretes utilized under marine environments was studied by mi-crohardness,SEM,XRD,MIP and 2 9 Si MAS NMR.The results showed that concrete under marine environ-ments is apt to be destroyed by dissolution or expansion damage due to the roles of gypsum and ettringite easily gathering in interface transition zone.Slag-incorporated Concrete is obviously less porous and the mechanical properties of the interface transition zone are enhanced.However,with the slag content of more than 30%,the pore refining effect is less significant and the distribution of pore diameter is bipolarized,the harmless pores and much harm pores are obviously increased,while harmful pores and less harm pores are reduced.There exist [SiO 4 ]tetrahedrons of hydration products in forms of Q3 and Q4 in addition to the forms of Q1 ,Q2 and Q2 (1Al),which can be resulted from the reduced resonance frequency of 2 9 Si and the chemical shift with a shift to negative.
参考文献
| [1] | I.G. Richardson .The calcium silicate hydrates[J].Cement and Concrete Research,2008(2):137-158. |
| [2] | DING Qingjun,HU Chenguang,FENG Xiaoxin,HUANG Xiulin.Effect of Curing Regime on the Distribution of Al3+Coordination in Hardened Cement Pastes[J].武汉理工大学学报（材料科学版）（英文版）,2013(05):927-933. |
| [3] | 胡晨光,丁庆军,胡曙光,封孝信.变温下SO2-4对水泥硬化浆体中Al3+配位分布的影响[J].功能材料,2014(02):2142-2146. |
| [4] | M. Vandamme;F.-J. Ulm.Nanoindentation investigation of creep properties of calcium silicate hydrates[J].Cement and Concrete Research,2013:38-52. |
| [5] | 刘子键,郑晓宁,刁波.疲劳荷载与海水侵蚀作用下钢筋混凝土梁耐久性试验[J].建筑结构学报,2014(03):171-177. |
| [6] | Majid Safehian;Ali Akbar Ramezanianpour .Assessment of service life models for determination of chloride penetration into silica fume concrete in the severe marine environmental condition[J].Construction and Building Materials,2013(Nov.):287-294. |
| [7] | S. Mahmoud Abdelkader;E. Reyes Pozo;A. Moragues Terrades .Evolution of microstructure and mechanical behavior of concretes utilized in marine environments[J].Materials & design,2010(7):p.3412. |
| [8] | Harvey H;Robert O N;Matha P K .Concrete deteriora-tion from physical attack by salts[J].Conerete Intem-ational,1996,18(01):63-68. |
| [9] | Nehdi M L;Suleiman A R;Soliman A M .Investigation of concrete exposed to dual sulfate attack[J].Cement and Concrete Research,2014,64(10):42-53. |
| [10] | Mindess S;Young J F;Wu Keru Darwin D.Con-crete(2nd ed)[M].北京:化学工业出版社,2005:426-430. |
| [11] | 李华,孙伟,左晓宝.矿物掺合料改善水泥基材料抗硫酸盐侵蚀性能的微观分析[J].硅酸盐学报,2012(08):1119-1126. |
| [12] | Zhang Gaozhan;Ding Qingjun;Gong Zicheng et al.Hy-dration process,composition and microstructure of slag-cement paste blends containing 0-70 % slag at different curing temperatures[J].Asian Journal of Chemistry,2013,26(05):1537-1539. |
| [13] | Bonen David;Cohen Menashi D .Magnesium sulfate at-tack on portland cement paste Ⅱ.Chemical and mineral analysis[J].Cement and Concrete Research,1992,22(02):707-718. |
| [14] | Ma Kunlin .Mechanism and evaluation method of salt crystallization attack on concrete[D].Changsha:Central South University,2009. |
| [15] | Frank Bellmann;Bernd Moser;Jochen Stark .Influence of sulfate solution concentration on the formation of gypsum in sulfate resistance test specimen[J].Cement and Concrete Research,2006(2):358-363. |
| [16] | Marchand J;Skalny J P;Ivan Odler.Sulfate attack on concrete[M].London:Spon Press,2001 |
| [17] | Renaudin G;Kubel F;Rivera J P et al.Structural phase transition and high temperature phase structure of Friedels salt,3CaO @ Al2O 3 @ CaCl2 @ 10H 2O[J].Ce-ment and Concrete Research,1999,29(12):1937-1942. |
| [18] | Duthil J P;Mankowski G;Giusti A .The synergetic effect of chloride and sulphate on pitting corrosion of copper[J].Corrosion Science,1996,38(10):1839-1849. |
| [19] | Xu Y .The influence of sulphates on chloride binding and pore solution chemistry[J].Cement and Concrete Re-search,1997,27(12):1841-1850. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%