采用超声辅助复乳法制备多孔 H AP 微球,通过调节反应温度、时间和 pH 值条件,获得了粒径分布均匀、形貌规则,具有不规则纳米多孔结构的 H AP微球。通过XRD、IR、SEM、TEM对微球进行了表征,研究了实验条件对产物成分及形貌的影响。结果表明,适宜的合成条件为：反应温度50℃,反应时间24 h,内水相pH 值≥10,在此条件下制备的产物为球形 HAP 粒子,直径分布在50~200 nm 之间,尺寸比较均一,每个微球由大量的纳米 H AP 粒子堆积而成,微球呈现疏松多孔结构。这种多孔 H AP 微球在骨组织修复及药物控释材料方面具有应用前景。
Porous hydroxyapatite(HAP)microspheres were prepared by a multiple emulsion method assisted by ultrasonic.With uniform size and irregular nano-pores of porous HAP microspheres were prepared by adj usting the factors of reaction temperature,time and pH value.The obtained microspheres were characterized using XRD,IR,SEM and TEM,and the experiment conditions on the product composition and morphology were studied.Results showed that the optimal temperature was 50 ℃,reaction time was 24 h,and the pH value of the inner water phase was over 10.The prepared HAP microspheres deposited with nano HAP particles are por-ous and have an average diameter of 50-200 nm.These porous HAP microspheres with an internal cavity are promising candidates for filler of skeletal defects and drug delivery.
参考文献
| [1] | B. Palazzo;M.C. Sidoti;N. Roveri;A. Tampieri;M. Sandri;L. Bertolazzi;F. Galbusera;G. Dubini;P. Vena;R. Contro .Controlled drug delivery from porous hydroxyapatite grafts: An experimental and theoretical approach[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2005(2):207-213. |
| [2] | Singh S;Bhardwaj P;Singh V;Aggarwal S;Mandal UK .Synthesis of nanocrystalline calcium phosphate in microemulsion - effect of nature of surfactants[J].Journal of Colloid and Interface Science,2008(1):322-329. |
| [3] | Saxena A;Kumar A;Mozumdar S .Preparation of calci-um phosphate nanostructures using reverse microemulsion method[J].Colloids and Surfaces A-Physicochemical and Engineering Aspects,2005,17(10):2765-2770. |
| [4] | Suchanek W.;Yoshimura M. .Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants [Review][J].Journal of Materials Research,1998(1):94-117. |
| [5] | Cosijns A;Vervaet C;Luyten J;Mullens S;Siepmann F;Van-Hoorebeke L;Masschaele B;Cnudde V;Remon JP .Porous hydroxyapatite tablets as carriers for low-dosed drugs.[J].European journal of pharmaceutics and biopharmaceutics: official journal of Arbeitsgemeinschaft fuer Pharmazeutische Verfahrenstechnik e.V,2007(2):498-506. |
| [6] | 张文龙,刘燕燕,李永绣,蒋柏泉.碳酸钙磷酸化工艺制备多孔球形羟基磷灰石[J].过程工程学报,2006(01):37-41. |
| [7] | 赵颖,徐为,姚爱华,黄文旵.多孔羟基磷灰石微球的原位转化制备研究[J].功能材料,2010(07):1124-1126. |
| [8] | Wang Q;Huang WH;Wang DP;Darvell BW;Day DE;Rahaman MN .Preparation of hollow hydroxyapatite microspheres[J].Journal of Materials Science. Materials in Medicine,2006(7):641-646. |
| [9] | 邵锋伟,蔡玉荣,姚菊明.多孔羟基磷灰石纳米球作为抗坏血酸载体的研究[J].高等学校化学学报,2010(06):1093-1097. |
| [10] | 刘莹,赵旭,潘琰,赵敬哲,王子忱.简单方法制备羟基磷灰石中空微球[J].物理化学学报,2009(07):1467-1471. |
| [11] | 罗德福,赵康,汤玉斐,马楚凡.羟基磷灰石空心微球的制备及其释药性能[J].硅酸盐通报,2010(03):651-656. |
| [12] | Mizushima Y;Ikoma T;Tanaka J;Hoshi K;Ishihara T;Ogawa Y;Ueno A .Injectable porous hydroxyapatite microparticles as a new carrier for protein and lipophilic drugs[J].Journal of Controlled Release: Official Journal of the Controlled Release Society,2006(2):260-265. |
| [13] | Isao KIMURA;Tatsuro HONMA and Richard E.RIMAN .Preparation of Hydroxyapatite Microspheres by Interfacial Reaction in a Multiple Emulsion[J].日本セラミックス协会学术论文志,2007(1348):888-893. |
| [14] | Chen B H;Chen K I;Ho Meiling et al.Synthesis of calcium phosphates and porous hydroxyapatite beads prepared by emulsion method[J].Materials Chemistry and Physics,2009,113(01):365-371. |
| [15] | Mizushima Y;Ikoma T;Tanaka J;Hoshi K;Ishihara T;Ogawa Y;Ueno A .Injectable porous hydroxyapatite microparticles as a new carrier for protein and lipophilic drugs[J].Journal of Controlled Release: Official Journal of the Controlled Release Society,2006(2):260-265. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%