氢氧化镁作为一种无卤阻燃剂，在聚合物阻燃领域具有重要的前景。采用反向沉淀法制得纳米级氢氧化镁粉体，研究了氯化镁添加方式对氢氧化镁粒度分布及团聚状态的影响，并通过热红外联用技术对其热解规律进行了分析。实验结果表明，氯化镁添加方式对氢氧化镁粒度分布及团聚状态有显著的影响；分4次加入氯化镁溶液所得氢氧化镁的粒度分布最均匀，小粒子所占的比例最大，不容易发生团聚现象。
Magnesium has an important prospect in the field of polymer flame retardant as a kind of halogen-free flame retardant.The nanoscale magnesium hydroxide powder was prepared by Reverse precipitation,the effect of the means of adding MgCl2 was studied on the particle size distribution and reunited state of Mg (OH)2 ,and the pyrolysis regularity of Mg (OH)2 was analyzed by the thermal infrared detection technology.The experi-mental results show that the means of adding MgCl2 has a significant effect on the distribution and reunited state of Mg(OH)2;the size distribution of Mg(OH)2 was the most homogeneous by four times to add for MgCl2 ,the proportion of small particles is the largest,and the reunion phenomenon is not easy to happen.
参考文献
| [1] | 蒋文俊,李哲曌,张春祥,方劲,杨绪杰,陆路德,刘孝恒.改性氢氧化镁的制备及在PA66中的阻燃应用[J].功能材料,2010(03):527-530. |
| [2] | 潘杰,李斌,王兆波,杜芳林.SiO2/Mg（OH）2复合阻燃剂的阻燃性能研究[J].功能材料,2012(01):6-9. |
| [3] | Qiu L Z;Xie R C;Ding P et al.Preparation and charac-terization of Mg(OH)2 nanoparticles and flame-retardant property of its nanocomposites with EVA[J].Compos-ites Structure,2003,62:391-395. |
| [4] | Hu Qingfu;Liu Hongyan;Wang Jinge et al.One-step technology of flame retardant magnesium hydroxide[J].Modern Chemical Industry,1988,3:22-24. |
| [5] | Gao Guiping;Li Sufen .Mg(OH)2 is manufactured by the continuous precipitation process of Brine-ammonia meth-od[J].Sea-lake Salt and Chemical Industry,1996,25(2):5-7. |
| [6] | 王雪松,叶俊伟,庞洪昌,贡卫涛,林源,宁桂玲.水镁石基有机无机复合阻燃剂的制备及应用[J].功能材料,2010(12):2124-2127. |
| [7] | 易求实.反向沉淀法制备纳米Mg（OH）2阻燃剂的研究[J].化学试剂,2001(04):197-199,228. |
| [8] | 王荣涛,梁小平,王小会,彭瑛,李建新,何本桥.纳米镁铝水滑石的制备及其对聚氨酯阻燃性能的影响[J].功能材料,2009(12):2119-2122. |
| [9] | 李秋菊,刘华彦,卢晗锋,郑敏珠,谢晶,陈银飞.pH值对氢氧化镁晶体生长的影响[J].材料科学与工程学报,2007(04):609-611,619. |
| [10] | 戴焰林,洪玲,施利毅.沉淀-共沸蒸馏法制备纳米Mg（OH）2的研究[J].上海大学学报(自然科学版),2003(05):402-404,409. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%