以水玻璃为硅源，煤油为分散介质，采用微乳液法和常压干燥工艺制备出了高比表面积、颗粒均匀的Si O 2超疏水性纳米粉体气凝胶，研究了微乳液形成所需表面活性剂的剂量范围、干燥时间及气凝胶粉体密度变化规律，并对制得气凝胶粉体的粒径分布、比表面积、微观形貌及疏水性进行了分析测试。结果表明，微乳液法制备所得气凝胶粉体粒径分布均匀，效率高，并具有良好的超疏水性能。
SiO2 nanopowder aerogel was prepared using silicon source of water glass and dispersion of medium kerosene by microemulsion method in ambient pressure dying process to prepare.The aerogel has good proper-ties of high specific surface area,uniform particles,and super-hydrophobic.Surfactant weight,dying time,and the density of the aerogel power were investigated.Also this study researched the particle size,specific surface area,morphology and hydrophobicity.Results show that the aerogel powder prepared by microemulsion method has the superiorities of uniform particle size,high efficiency and super-hydrophobic.
参考文献
| [1] | Horiuchi T.;Osaki T.;Sugiyama T.;Suzuki K.;Mori T.;Chen L. .A novel alumina catalyst support with high thermal stability derived from silica-modified alumina aerogel[J].Catalysis Letters,1999(2/3):89-92. |
| [2] | Bi Yutie;Ren Hongbo;Chen Bowei et al.Synthesis and characterization of nickel-based aerogel[J].Journal of Functional Materials,2012,43(11):1361-1363. |
| [3] | 史亚春,李铁虎,王习林,刘和光,吕婧,张智广.SiO2气凝胶/中间相沥青基泡沫炭复合材料的制备与表征[J].功能材料,2013(20):3049-3052. |
| [4] | Hirashima H;Kojima C;Imai H .Application of alumina aerogels as catalysts[J].Journal of Sol-Gel Science and Technology,1997,8(1-3):843-846. |
| [5] | Smirnova I;Suttiruengwong S;Arlt W .Feasibility study of hydrophilic and hydrophobic silica aerogels as drug delivery systems[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(0):54-60. |
| [6] | A. Parvathy Rao;A. Venkateswara Rao;G.M. Pajonk .Hydrophobic and physical properties of the ambient pressure dried silica aerogels with sodium silicate precursor using various surface modification agents[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(14):6032-6040. |
| [7] | Kistler S S .Coherent expanded aerogels and jellies[J].NATURE,1931,127:741. |
| [8] | Baumann, TF;Gash, AE;Chinn, SC;Sawvel, AM;Maxwell, RS;Satcher, JH .Synthesis of high-surface-area alumina aerogels without the use of alkoxide precursors[J].Chemistry of Materials,2005(2):395-401. |
| [9] | Sarawade P B .Synthesis and characterization of microme-ter-sized silica aerogel nanoporous beads[J].Materials Letters,2012,81(10):37-40. |
| [10] | Kim SM;Lee YJ;Jun KW;Park JY;Potdar HS .Synthesis of thermo-stable high surface area alumina powder from sol-gel derived boehmite[J].Materials Chemistry and Physics,2007(1):56-61. |
| [11] | 陈小兵,余双平,邓淑华,黄慧民,周立清.纳米粉体干燥方法的研究进展[J].无机盐工业,2004(01):7-9. |
| [12] | Zhang K.;Kawi S.;Wang J.;Gan LM.;Chew CH. .Synthesis and evaluation of a ruthenium-copper oxide/silica catalyst derived from microemulsion processing[J].Catalysis Letters,2000(2/4):179-184. |
| [13] | Bhagat, SD;Kim, YH;Ahn, YS;Yeo, JG .Textural properties of ambient pressure dried water-glass based silica aerogel beads: One day synthesis[J].Microporous and Mesoporous Materials,2006(1/3):237-244. |
| [14] | Pi H T;Hu S J .Transparent water-in-oil dispersions:the oleopathic hydro-micelle[J].NATURE,1943,152(3847):102-103. |
| [15] | Pradip B. Sarawade;Jong-Kil Kim;Askwar Hilonga .Production of low-density sodium silicate-based hydrophobic silica aerogel beads by a novel fast gelation process and ambient pressure drying process[J].Solid state sciences,2010(5):911-918. |
| [16] | 何方,熊先文,吴菊英,黄渝鸿,张瑞珠,邹文俊,彭进,马秋花,朱贺,李荣春.SiO2气凝胶微球的雾化制备及表征[J].功能材料,2013(01):143-146. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%