以马来酸酐(MAH)和丙烯酸丁酯(BA)为单体,通过溶液接枝法制备了聚乳酸(PLA )接枝MAH/BA共聚物(mPLA).使用红外光谱(FT-IR)、广角X 射线衍射(WAXD)、差示扫描量热仪(DSC)、热重分析仪(TG)研究了接枝共聚物的结构和性能.结果表明,随着单体质量比BA/MA H 的增加,单体在PLA 上的接枝率出现先增大后减小的趋势,当m(MAH)/m (BA )＝1/1,m (MAH )/m (PLA )＝3/100时,制备的 mPLA 接枝率最高为1．96％；与纯PLA相比,mPLA 的结晶度和热稳定性均比有所下降,且样品的接枝率越大其结晶度越低；随着单体中BA含量的增加,mPLA 的熔融温度和玻璃化转变温度有减小的趋势.
Maleic anhydride (MAH)/butyl acrylate (BA)grafted poly(lactic acid)(PLA)copolymers (mPLAs) were prepared through solution grafting copolymerization using benzoyl peroxide as initiator,MAH and BA as monomers.The structure and properties of the graft copolymers were characterized by Fourier transform infra-red spectroscopy (FT-IR),wide-angle X-ray diffraction (WAXD),differential scanning calorimetry (DSC)and thermogravimetry (TG).The monomer graft degree on PLA first increases and then decreases with increasing mass ratio of BA to MAH.It reaches the highest value of 1.96% when the mass ratios of BA to MAH and MAH to PLA are 1/1 and 3/100 respectively.Compared with the pure PLA,mPLAs exhibit lower crystallinity and decreased thermal stability.A higher monomer graft degree was associated with a lower crystallinity of the samples.With the increase of mass ratio of BA to MAH,both the melting temperature and glass transition temperature of mPLAs have a trend of declining.
参考文献
| [1] | Rahul M. Rasal;Amol V. Janorkar;Douglas E. Hirt .Poly(lactic acid) modifications[J].Progress in Polymer Science,2010(3):338-356. |
| [2] | S. Pavlidou;C.D. Papaspyrides .A review on polymer-layered silicate nanocomposites[J].Progress in Polymer Science,2008(12):1119-1198. |
| [3] | 徐阳,孙志丹,陈晓浪,郭刚,张志斌,胡书春.结晶温度对左旋聚乳酸的晶体改性和晶体形貌的影响[J].功能材料,2012(16):2138-2141. |
| [4] | K.P. Pramoda;C.B. Koh;H. Hazrat .Performance Enhancement of Polylactide by Nanoblending With POSS and Graphene Oxide[J].Polymer Composites,2014(1):118-126. |
| [5] | Mujtahid Kaavessina;Ilias Ali;Rabeh Elleithy .Preparation and characterization of poly(lactic acid)/ elastomer blends prepared by melt blending technique[J].Journal of Elastomers & Plastics,2014(3):253-268. |
| [6] | 严好,潘君,江伟民,张晓喜,王远亮.一种生物素改性聚乳酸生物材料的制备与性能研究[J].功能材料,2011(03):399-403. |
| [7] | Okuda, T.;Ishimoto, K.;Ohara, H.;Kobayashi, S. .Renewable biobased polymeric materials: Facile synthesis of itaconic anhydride-based copolymers with poly(l -lactic acid) grafts[J].Macromolecules,2012(10):4166-4174. |
| [8] | Abolfazl Zare;Mohammad Morshed;Rouhollah Bagheri .Effect of Various Parameters on the Chemical Grafting of Amide Monomers to Poly(lactic acid)[J].Fibers and Polymers,2013(11):1783-1793. |
| [9] | Themistou E;Battaglia G;Armes S P .Facile synthesis of thiol-functionalized amphiphilic polylactide-methacrylic diblock copolymers[J].Polymer Chemistry,2014,5(4):1405-1417. |
| [10] | R. Dorati;C. Colonna;C. Tomasi;I. Genta;G. Bruni;B. Conti.Design of 3D scaffolds for tissue engineering testing a tough polylactide-based graft copolymer[J].Materials science & engineering, C. Materials for Biogical applications,2014:130-139. |
| [11] | The effect of crystallization of PLA on the thermal and mechanical properties of microfibrillated cellulose-reinforced PLA composites[J].Composites science and technology,2009(7/8):1187-1192. |
| [12] | Wu, CS .Renewable resource-based composites of recycled natural fibers and maleated polylactide bioplastic: Characterization and biodegradability[J].Polymer Degradation and Stability,2009(7):1076-1084. |
| [13] | Wang Huimin;Chou Yiting;Wu Chinsan et al.Polyes-ter/cellulose acetate composites:preparation,character-ization and biocompatible[J].Journal of Applied Poly-mer Science,2012,126(s1):E242-E251. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%