以二月桂酸二丁基锡(T-12)为催化剂,通过异佛尔酮二异氰酸酯(IPDI ),聚四氢呋喃二醇(PTMG1000),二羟甲基丁酸(DMBA)、γ-氨丙基三乙氧基硅烷(γ-APTES)和环氧树脂(E-44)的反应制备了醇溶性羟基封端聚氨酯(EPPU).采用傅立叶变换红外光谱(FT-IR )、X 射线衍射(XRD )、透射电镜(TEM)和扫描电镜(SEM)对聚氨酯的结构进行了表征,并测试了环氧树脂含量w(E-44)对胶膜的耐热性、力学性能和耐水性的影响.FT-IR测试结果表明环氧树脂与聚氨酯发生了反应,实现了化学改性.环氧改性使聚氨酯的结晶度下降,同时热稳定性和机械性能得到改善.当w(E-44)从0％(质量分数)提高到10％(质量分数),改性使聚氨酯的拉伸强度从5．19~6．99 MPa,吸水率从19．81％降低至4．865％.
Hydroxyl-terminated polyurethane modified by epoxy resin(EPPU)was prepared by the reaction of isophorone diisocyanate (IPDI),poly (tetramethylene glycol)(PTMG),2,2-dimethylolbutanoic acid(DMBA),γ-Aminopropyl triethoxysilane(γ-APTES),phoenix epoxy resin(E-44)and dibutyltindilaurate (T-12)as cata-lyst.The structure of the polyurethane was characterized by Fourier transform infrared (FT-IR)spectrometer, X-ray diffraction (XRD)and transmission electron microscope(TEM).The effect of E-44 content on thermal stability,mechanical properties and water absorption of the membranes were measured.FT-IR indicates that epoxy resin has been successfully introduced into the polymer main chain,and XRD shows that crystallinity of EPPU decreased with the addition of epoxy resin while the thermal stability has been improved.It was found that better mechanical properties of polyurethane were obtained when chemical networks formed after modifica-tion by epoxy resin.As the w(E-44)increases from 0% to 10%,the tensile strength increased from 5.19 to 6.99 MPa and the water absorption of the membranes decreased from 19.81% to 4.865%.
参考文献
| [1] | Yongshang Lu;Richard C. Larock .New Hybrid Latexes from a Soybean Oil-Based Waterborne Polyurethane and Acrylics via Emulsion Polymerization[J].Biomacromolecules,2007(10):3108-3114. |
| [2] | Lai, X.;Song, Y.;Liu, M. .Preparation and application of cationic blocked waterborne polyurethane as paper strength agent[J].Journal of Polymer Research,2013(8):222-1-222-6. |
| [3] | 杜媛,李小瑞,赖小娟,王小荣.磺酸型水性聚氨酯胶粘剂的制备及性能研究[J].功能材料,2013(18):2680-2683. |
| [4] | Van-Landuyt KL;Snauwaert J;De-Munck J;Peumans M;Yoshida Y;Poitevin A;Coutinho E;Suzuki K;Lambrechts P;Van-Meerbeek B .Systematic review of the chemical composition of contemporary dental adhesives.[J].Biomaterials,2007(26):3757-3785. |
| [5] | Xiang Liu;Fan Xiaodong;Tang Minfeng et al.Synthesis and characterization of core-shell acrylate based latex and study of its reactive blends[J].INTERNATIONAL JOURNAL OF MOLECULAR SCIENCES,2008,9(3):342-354. |
| [6] | Brostow, W.;Dutta, M.;Rusek, P. .Modified epoxy coatings on mild steel: Tribology and surface energy[J].European Polymer Journal,2010(11):2181-2189. |
| [7] | Alarcia F;de la Cal J C;Asua J M .Continuous produc-tion of specialty waterborne adhesives:tuning the adhe-sive performance[J].CHEMICAL ENGINEERING JOURNAL,2006,122(3):117-126. |
| [8] | Sardon, H.;Irusta, L.;Fernández-Berridi, M.J.;Lansalot, M.;Bourgeat-Lami, E. .Synthesis of room temperature self-curable waterborne hybrid polyurethanes functionalized with (3-aminopropyl)triethoxysilane (APTES)[J].Polymer: The International Journal for the Science and Technology of Polymers,2010(22):5051-5057. |
| [9] | Bai CY;Zhang XY;Dai JB;Zhang CY .Water resistance of the membranes for UV curable waterborne polyurethane dispersions[J].Progress in Organic Coatings: An International Review Journal,2007(4):331-336. |
| [10] | Anand Prabu A;Alagar M .Mechanical and thermal studies of intercross-linked networks based on sili-conized and polyurethane-epoxy/unsaturated polyester coatings[J].Progress in organic Coatings,2004,49(3):236-243. |
| [11] | Qingming Jia;Maosheng Zheng;Renjie Shen;Hongxiang Chen .Synthesis,characterization and properties of organoclay-modified polyurethane/epoxy interpenetrating polymer network nanocomposites[J].Polymer international,2006(3):257-264. |
| [12] | Magalad V T;Gokavi G S;Raju K V S N et al.Mixed matrix blend membranes of poly(vinyl alcohol)-poly(vi-nyl pyrrolidone)loaded with phosphomolybdic acid used in pervaporation dehydration of ethanol[J].Journal of Membrane Science,2010,354(1-2):150-161. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%