采用30 g/L的含氟和有机硅拒水剂分别对织物先进行拒水整理，再对拒水整理的织物进行夜光涂层，讨论两种不同拒水剂整理对夜光涂层织物的牢度性能、发光性能、耐水洗性能、防水透湿透气性能以及表面形态的影响。结果显示，未经拒水整理的夜光涂层织物的牢度、发光性能和透湿性比经拒水整理的要好，但是耐水洗、透气性和拒水性能要差；有机硅拒水剂整理的夜光涂层织物的牢度、发光性能、耐水洗性和透湿性均比含氟拒水剂整理的要好，但是透气性和拒水性均不如含氟拒水剂整理的夜光涂层织物。
Have a water repellent finish on fabric by using fluoride from water and organic silicon from agent re-spectively setting the concentration at 30 g/L firstly,and then coated with luminous materials.Discuss the influ-ence of two different repellent finishing agents on the coated fabric’s fastness,luminous property,washing prop-erty,waterproof property,moisture permeation property,breathability property and surface morphology.The results show that luminous coated fabric has no water repellent finish was better at fastness luminance and moisture permeation than that has,but show worse at washing,water resistance and breathability.Luminous coated fabric that has be finshed by organic silicon from agent was better at fastness,luminance,washing and moisture permeation than that has be finshed by fluoride from water,but do worse at water resistance and breathability.
参考文献
| [1] | Xing Fenglan;Xu Qun.Printing and dyeing auxiliary[M].北京:化学工业出版社,2002:266-282. |
| [2] | 董朝红,吕洲,朱平.反应型含磷氮元素的聚硅氧烷的制备及其对棉织物拒水阻燃性能研究[J].功能材料,2013(18):2601-2606. |
| [3] | Dong Yongchun.Assistant agents in textile[M].Shanghai:Donghua University Press,2009:226-228. |
| [4] | 王薇,施秋萍,朱泉.含氟整理剂WR-1在锦纶织物上的应用[J].印染,2009(16):33-35. |
| [5] | Kang Wei;Ye Shuhui .The test methods of nano clothes' water and oil-repellent performance[J].Knitting Indus-tries,2012,7(28):97-99. |
| [6] | 杜文琴,徐杰.针织阻燃涂层织物的研制及其性能[J].纺织学报,2012(01):92-95. |
| [7] | 黄小华,石小奕,赵堃.织物拒水拒油整理工艺探讨[J].安徽工程大学学报,2012(03):21-23,26. |
| [8] | Luo Ruilin.Fabric coating technology[M].Beijing:China Textile Press,2005:81-91. |
| [9] | Zhao X;Stylios GK;Christie RM .Rheological behavior of polymer solutions during fabric coating[J].Journal of Applied Polymer Science,2008(4):2317-2321. |
| [10] | S.FARBOODMANESH;J.CHEN;J.L.MEAD;K.D.WHITE;H.E.YESILALAN .Effect of Coating Thickness and Penetration on Shear Behavior of Coated Fabrics[J].Journal of Elastomers & Plastics,2005(3):197-227. |
| [11] | Zhu Yanan;Wu Min;Li Weizhen et al.Influence of acrylic ester adhesive on luminous coating fabric per-formance[J].Dyeing and Finishing,2011,37(14):27-29. |
| [12] | 徐燃霞,葛明桥.蓄能型夜光织物的开发及应用[J].江南大学学报(自然科学版),2004(02):184-187. |
| [13] | Sun Yanbin;Qiu Guanming;Zhang Shengqu et al.SrAl2 O4:Eu3+,Dy3+ long afterglow phosphors pre-pared by chemical comprecipitation method[J].Journal of Rare Earths,2004,22(2):29-33. |
| [14] | Wang Jian;Li Yonggui;Zhu Yanan et al.Effect of sof-tening finishing on the performance of a luminous coa-ted fabric[J].Journal of Textile Research,2013,34(9):99-102. |
| [15] | Yu Weidong.Textile materials[M].Beijing:China Textile Press,2006:329-334. |
| [16] | 徐旭凡,王善元.聚氨酯转移涂层织物的透湿防水性能[J].纺织学报,2005(03):82-84. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%