以丁二酸、丁二醇、1,6-己二胺为原料,二丁基二月桂酸锡为催化剂,甲苯二异氰酸酯(TDI)为扩链剂,通过熔融共聚,合成了 M w为40~65 k 的聚丁二酸-丁二醇-1,6-己二胺共聚物,并采用压延成膜法制得聚酯酰胺薄膜.研究了1,6-己二胺含量对聚酯酰胺的热性能、结晶性能、降解性能和流变性能的影响.结果表明,合成了聚酯酰胺,其熔点达到100．97℃,热分解温度为317．85℃；随着1,6-己二胺添加量增加,聚酯酰胺的拉伸强度不断变大,断裂伸长率略有下降；1,6-己二胺的加入并未改变聚酯酰胺的晶型,但降低了其结晶度；1,6-己二胺的加入提高了聚酯酰胺降解性能,而且改善了其流变性能,这有利于聚酯酰胺的成型加工和应用.
Succinic acid-butanediol-1,6-hexamethylenediamine polyester amide copolymers with Mw from 40 000 to 65 000 were synthesized by succinic acid,1,4-butylene and 1,6-hexamethylenediamine,through high temper-ature melt reaction.Meanwhile,the second dibutyl tin laurate was selected as catalyst,and the toluene disocya-nate (TDI)was selected as chain extender.The succinic acid-butylene-adipic amine copolymer films were pre-pared by calendering film-forming method.The influences of the content of 1,6-adipic amine on the copolymer performance of thermal,crystallization,degradation and rheological properties were researched.The results showed that the polyester amide copolymers were synthesized successfully,whose melting point is 100.97 ℃and the thermal decomposition temperature is 317.85 ℃.With the increasing of 1,6-adipic amine,the tensile strength of copolymers increased accordingly,and the elongation at break decreased slightly.1,6-adipic amine did not change the crystal type of copolymer,but the crystallinity of copolymer decreased.With adding the 1,6-adipic amine in copolymer,the degradation performance and rheological properties of the copolymers were im-proved,which is useful for the further processing.
参考文献
| [1] | Fonseca, A.C.;Coelho, J.F.J.;Valente, J.F.A.;Correia, T.R.;Correia, I.J.;Gil, M.H.;Sim?es, P.N. .Poly(ester amide)s based on (L)-lactic acid oligomers and α-amino acids: Influence of the α-amino acid side chain in the poly(ester amide)s properties[J].Journal of biomaterials science,2013(12):1391-1409. |
| [2] | Li XY;Sun J;Huang YJ;Geng Y;Wang X;Ma Z;Shao CG;Zhang X;Yang CL;Li LB .Inducing new crystal structures through random copolymerization of biodegradable aliphatic polyester[J].Macromolecules,2008(9):3162-3168. |
| [3] | Marija S.Nikolic;Jasna Djonlagic .Synthesis and characterization of biodegradable poly(butylene succinate-co-butylene adipate)s[J].Polymer Degradation and Stability,2001(2):263-270. |
| [4] | Xu J;Guo B H .Poly(butylene succinate)and its copoly-mers:research,development and industrialization[J].Bi-otechnology Journal,2010,5(11):1149-1163. |
| [5] | Lu, S-F.;Chen, M.;Shih, Y.-C.;Chen, C.H. .Nonisothermal crystallization kinetics of biodegradable poly(butylene succinate-co-propylene succinate)s[J].Journal of Polymer Science, Part B. Polymer Physics,2010(12):1299-1308. |
| [6] | Nagata M. .Synthesis and enzymatic degradation of poly(tetramethylene succinate) copolymers with terephthalic acid[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(11):4373-4376. |
| [7] | Liu Y J;Xie W;Liu Y W;Liu P .Synthesis,characteriza-tion of adipic acid-1,4-butanediol-urea copolymer[J].Journal of Functional Materials,2012,43(16):2176-2180. |
| [8] | Li XY;Hong ZF;Sun J;Geng Y;Huang YJ;An HN;Ma Z;Zhao BJ;Shao CG;Fang YP .Identifying the Phase Behavior of Biodegradable Poly(hexamethylene succinate-co-hexamethylene adipate) Copolymers with FTIR[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,2009(9):2695-2704. |
| [9] | Montaudo G.;Rizzarelli P. .Synthesis and enzymatic degradation of aliphatic copolyesters[J].Polymer Degradation and Stability,2000(2):305-314. |
| [10] | Papageorgiou, GZ;Nanaki, SG;Bikiaris, DN .Synthesis and characterization of novel poly(propylene terephthalate-co-adipate)biodegradable random copolyesters[J].Polymer Degradation and Stability,2010(4):627-637. |
| [11] | Huang C Q;Xu S Y;Zhao J B;Jiang S L Yang W T .Synthsis and characterization of polyesteramides derived from aliphatic diesterdiamides[J].Acta Polymerica Sini-ca,2010,1(05):574-581. |
| [12] | Ihn KJ.;Im SS.;Yoo ES. .STRUCTURE AND MORPHOLOGY OF POLY(TETRAMETHYLENE SUCCINATE) CRYSTALS[J].Macromolecules,1995(7):2460-2464. |
| [13] | S.S. Umare;A.S. Chandure;R.A. Pandey .Synthesis, characterization and biodegradable studies of 1,3-propanediol based polyesters[J].Polymer Degradation and Stability,2007(3):464-479. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%