制备稳定的全氟烷基丙烯酸酯改性阳离子聚氨酯复合乳液，并通过红外和核磁共振氢谱对其结构进行表征。重点研究功能性单体全氟烷基丙烯酸酯(FA)用量及阳离子扩链剂 N-甲基二乙醇胺(MDEA)用量对复合乳胶膜性能的影响。力学性能分析表明， FA 用量对乳胶膜拉伸强度影响比较复杂；随 MDEA用量增大，乳胶膜拉伸强度增大。表面自由能分析表明随 FA、MDEA 用量增大，乳胶膜表面自由能降低。乳胶膜表面扫描电镜表明含氟乳胶膜表面光滑洁净，表面 EDS 能谱分析表明，随着 FA 及 MDEA 用量增大，氟原子更容易向膜表面迁移；乳胶膜断面扫描电镜表明随着 FA 及 MDEA 用量增大，乳胶膜断面呈规整的分层结构。
The perfluorinated acrylate modified cationic polyurethane (PUFA)hybrid emulsions were prepared and characterized by IR and 1 H NMR.The emphasis was put on the influence of the content of FA as functional monomer and the content of MDEA as cationic extender on the PUFA hybrid films properties.The mechanical property test results showed that the FA content had complex effects on the tensile strength of the PUFA films and the tensile strength of the PUFA films increased with the increasing MDEA content.The analysis indicated that the surface free energy of PUFA films decreased with the increase of the FA and MDEA content.SEM im-age showed that the surface of the PUFA films was smooth and clean.The EDS spectrum of PUFA films sur-face showed that the fluorine atoms were more likely to migrate to the film surface with the increase of the FA and MDEA content.SEM photos indicated that the PUFA films section had more regular layered structure with the increase of the FA and MDEA content.
参考文献
| [1] | Wang, Y.;Qiu, F.;Xu, B.;Xu, J.;Jiang, Y.;Yang, D.;Li, P. .Preparation, mechanical properties and surface morphologies of waterborne fluorinated polyurethane-acrylate[J].Progress in Organic Coatings: An International Review Journal,2013(5):876-883. |
| [2] | Min Jiang;Zhaohui Zheng;Xiaobin Ding .Convenient synthesis of novel fluorinated polyurethane hybrid latexes and core-shell structures via emulsion polymerization process with self-emulsification of polyurethane[J].Colloid and polymer science,2007(9):1049-1054. |
| [3] | Xiao Xinyan;Wang Ye .Emulsion copolymerization of fluorinated acrylate in the presence of a polymerizable e-mulsifier[J].Colloids and Surfaces A-Physicochemical and Engineering Aspects,2009,348(1-3):15 1-156. |
| [4] | Deng JN;Cao J;Li JH;Tan H;Zhang Q;Fu Q .Mechanical and surface properties of polyurethane/fluorinated multi-walled carbon nanotubes composites[J].Journal of Applied Polymer Science,2008(3):2023-2028. |
| [5] | 辛华,李小瑞,沈一丁.聚氨酯-含氟丙烯酸酯防水防油性复合乳液的制备及性能[J].功能材料,2011(03):474-478. |
| [6] | Jiang, GC;Tuo, XL;Wang, DR;Li, Q .Preparation, Characterization, and Properties of Fluorinated Polyurethanes[J].Journal of Polymer Science, Part A. Polymer Chemistry,2009(13):3248-3256. |
| [7] | Chen Kuoyu;Kuo Jenfeng .Synthesis and properties of novel fluorinated aliphatic polyurethanes with fluoro chain extenders[J].Macromolecular Chemistry and Physics,2010,201(18):2676-2686. |
| [8] | Claudio Tonelli;Tania Trombetta;Massimo Scicchitano et al.New perfluoropolyether soft segment containing polyurethane[J].Journal of Applied Polymer Science,1995,57(9):1031-1042. |
| [9] | 汪江节,陈建兵,王武生,曾俊.含氟丙烯酸酯改性水性聚氨酯涂饰剂的制备[J].皮革化工,2006(05):37-39. |
| [10] | Hua Xin;Yi-Ding Shen;Xiao-Rui Li .Synthesis and properties of cationic polyurethane-fluorinated acrylic hybrid latexes by emulsifier-free emulsion polymerization and the solvent-free method[J].Polymer bulletin,2011(9):1849-1863. |
| [11] | Chengcheng Yang;Valter Castelvetro;Yongming Zhang .Facile hydrophobic modification of hybrid poly(urethane-urea)methacrylate aqueous dispersions and films through blending with novel waterborne fluorinated acrylic copolymers[J].Colloid and polymer science,2012(6):491-506. |
| [12] | Xin, H.;Shen, Y.;Li, X. .Novel cationic polyurethane-fluorinated acrylic hybrid latexes: Synthesis, characterization and properties[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2011(1/3):205-211. |
| [13] | Liu SH;Zhu GQ .Effects of altered reaction conditions on the synthesis of polyurethane-poly(2,2,2-trifluoroethyl methacrylate) triblock copolymer aqueous dispersion[J].European Polymer Journal,2007(9):3904-3911. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%