针对ITER HCCB-TBM氚提取系统氚化水分解处理需求,考察了Zr30 Ni70合金在500℃下的吸氢特性和水分解反应前后的物相变化,并采用微型固定床反应器考察了不同粒度合金在500℃下对惰性气体中微量水的分解反应性能。结果表明,Zr30 Ni70合金吸氢量极低,满足Sievert定律；合金水分解的有效成分是 Zr,反应产物为ZrO2；合金粉体粒径越小,床层水分解的穿透容量越大；粉体造粒后可兼顾低床层压降和高穿透容量；水蒸汽浓度变化对穿透容量基本无影响,氢含量低于1％时对穿透容量无影响；当造粒颗粒床层高度超过120 mm,床层利用率＞98％。
In order to fulfill the requirement of tritiated water decomposition in tritium extraction system in ITER HCCB-TBM,Zr30 Ni70 was selected and the following performances at 500 ℃ were investigated:hydrogen absorption property,phase transformation in water decomposition process and trace water decomposition reac-tion in micro fixed-bed reactor.The results showed that the hydrogen absorption in alloy obeys to Sievert law with very low capactity,the effective element in alloy for water decomposition is Zr and the product is ZrO2 . The breakthrough capacity increased with the decrease of powder size,the granulation of powder with 400 mesh size could guarantee both high breakthrough capacity and low pressure drop,the breakthrough capacity didn’t change with the variety of water concentration and with the hydrogen concentration less than 1%,the utilization rate of bed exceeded 98% with the packing height larger than 120 mm.
参考文献
| [1] | C.A. Chen;D.L. Luo;Y. Sun;Z.Y. Huang;Y.F. Xiong.Tritium Safety Consideration In The Design Of Tritium Systems For China Hcsb And Dfll Tbms[J].Fusion engineering and design,200810/12(10/12):1455-1460. |
| [2] | Nishikawa M.;Kinjyo T.;Nishida Y..Chemical form of tritium released from solid breeder materials[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,20042/3(2/3):87-93. |
| [3] | Kang, C.;Wang, X.;Xiao, C.;Gao, X.;Gu, M.;Liu, J.;Wang, H.;Peng, S.;Chen, X..Out-of-pile tritium release study on Li_4SiO_4 pebbles from TRINPC-I experiments[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,20111(1):62-65. |
| [4] | I. Ricapito;A. Ciampichetti;P. Agostini;G. Benamati.Tritium Processing Systems For The Helium Cooled Pebble Bed Test Blanket Module[J].Fusion engineering and design,200810/12(10/12):1461-1465. |
| [5] | Luo Deli;Song Jiangfeng;Huang Guoqiang;Chen Chang-an;Huang Zhiyong;Deng Xiaojun;Oin Cheng;Qian Xiaojing;Zhang Guikai.Progress of China's TBM tritium technology[J].Fusion engineering and design,20127/8(7/8):1261-1267. |
| [6] | Diego Escobar;Sesha Srinivasan;Yogi Goswami.Hydrogen storage behavior of ZrNi 70/30 and ZrNi 30/70 composites[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20081/2(1/2):223-230. |
| [7] | Stanislaw M. Filipek;ValeriePaul-Boncour;Ru-Shi Liu.ZrNi5-based hydrogenated phases formed under high hydrogen pressure conditions[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,201119(19):8237-8240. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%