采用改进共沉淀法制备铁铈复合氧化物催化剂,通过 L16(45)正交实验确定最佳工艺条件.研究了不同煅烧温度对催化剂脱硝效率的影响,同时通过XRD、SEM、粒度和比表面积等方法对催化剂进行表征.结果表明,反应终点pH 值是碳酸氢铵-氨水沉淀法制备铁铈催化剂最重要的影响因素,反应温度次之.脱硝实验表明,经400℃焙烧5 h所制备的催化剂,其粒径较小,分布较宽,比表面积较大,SCR 脱硝活性最高,在250℃脱硝活性为93．8％.
The preparation process of catalyst composited with Fe-Ce oxides was studied by improved co-precipi-tation.The optimum conditions were determined by L16 (45 )orthogonal test.The effects of different calcination temperature on SCR of Fe-Ce catalyst were studied,and also the materials were characterized by XRD,SEM, particle size and specific surface area.The results show that the final pH of the reaction is the most important factor for Fe-Ce catalyst precipited from bicarbonate-ammonia system.Reaction temperature is the secondary factor.The denitration experiments showed that catalyst prepared by roasting at 400 ℃ for 5 h with smaller particle size,wider distribution,larger specific surface area and the highest SCR denitration activity.The activi-ty was 9 3 .8% at 2 5 0 ℃.
参考文献
| [1] | 贺媛媛;刘清才;席文昌;许志鹏;杨剑;杨强;孙亚丽.WO_3添加方式对V_2O_5/TiO_2催化剂性能影响[J].功能材料,2012(16):2231-2234. |
| [2] | 杨眉;刘清才;薛屺;高英.化学气相沉积制备V2O5-WO3/TiO2催化剂及表征[J].功能材料,2010(4):683-686. |
| [3] | Long R.Q..The promoting role of rare earth oxides on Fe-exchanged TiO_2-pillared clay for selective catalytic reduction of nitric oxide by ammonia[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,20002(2):87-95. |
| [4] | Fudong Liu;Hong He;Yun Ding.Effect of manganese substitution on the structure and activity of iron titanate catalyst for the selective catalytic reduction of NO with NH3[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,20091/2(1/2):194-204. |
| [5] | The activity and characterization of CeO_2-TiO_2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH_3[J].Journal of hazardous materials,20101/3(1/3):734. |
| [6] | Hai Zhao;Dexiang Zhang;Fangfang Wang.Modification of ferrite-manganese oxide sorbent by doping with cerium oxide[J].Transactions of The Institution of Chemical Engineers. Process Safety and Environmental Protection, Part B,20086(6):448-454. |
| [7] | 陈亮;李俊华;葛茂发;马磊;常化振.CeO2-WO3复合氧化物催化剂的NH3-SCR反应机理[J].催化学报,2011(5):836-841. |
| [8] | 陈燕;李彩亭;曾光明;樊小鹏.Ce-Fe/ACF催化剂低温选择性催化还原NO的研究[J].环境工程学报,2010(3):625-628. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%