使用N-乙酰-D-氨基葡萄糖作为碳源,F127作为软模板,乙酸钴作为钴源和催化剂,在水热和高温热解条件下制得了具有较大的比表面积与丰富的介孔尺寸的孔道结构、尺寸为200~500 nm的氧化钴/氮掺杂复合介孔碳球.该复合介孔碳球用作电极材料进行电化学测试,在2 A/g 的电流密度下电容值达到248．75 F/g,经过1000次循环寿命测试后其比电容值还能保留93％,显示出较高的比电容值和较好的循环稳定性,有望在能源存储、催化、吸附等领域得到应用.
The cobalt oxide/nitrogen-doped mesoporous composite carbon spheres with a size of 200-500 nm were obtained after hydrothermal and pyrolysis approach using N-Acetyl-D-glucosamine as carbon source,F127 as soft template,cobalt acetate as cobalt source and catalyst.N-Acetyl-D-glucosamine can self-assemble with F127 and cobalt acetate through the effect of hydrogen bonding.The obtained mesoporous carbon sphere exhib-its a large surface area and abundant mesoporous pore structure.The composite mesoporous carbon sphere was applied as an electrode material and found to exhibit a high specific capacitance of 248.75 F/g at the current den-sity of 2 A/g.Its capacitance can still remain 93% after 1 000 cycle charge and discharge progress which reveals a good cyclic stability.Owning to the excellent performance,the cobalt oxide/nitrogen-doped mesoporous car-bon spheres have the potential applications in energy storage,catalysis and adsorption.
参考文献
| [1] | 王六平;周颖;邱介山.硝酸氧化对沥青烯基有序介孔炭电化学性能的影响[J].新型炭材料,2011(3):204-210. |
| [2] | X.L. Chen;W.S. Li;C.L. Tan;W. Li;Y.Z. Wu.Improvement In Electrochemical Capacitance Of Carbon Materials By Nitric Acid Treatment[J].Journal of Power Sources,20082(2):668-674. |
| [3] | Li Zhao;Li-Zhen Fan;Meng-Qi Zhou;Hui Cuan;Suyan Qiao;Markus Antonietti;Maria-Magdalena Titirici.Nitrogen-Containing Hydrothermal Carbons with Superior Performance in Supercapacitors[J].Advanced Materials,201045(45):5202-5206. |
| [4] | Zhenhai Wen;Xinchen Wang;Shun Mao;Zheng Bo;Haejune Kim;Shumao Cui;Canhua Lu;Xinliang Feng;Junhong Chen.Crumpled Nitrogen-Doped Graphene Nanosheets with Ultrahigh Pore Volume for High-Performance Supercapacitor[J].Advanced Materials,201241(41):5610-5616. |
| [5] | Jens Peter Paraknowitsch;Arne Thomas;Markus Antonietti.A detailed view on the polycondensation of ionic liquid monomers towards nitrogen doped carbon materials[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,201032(32):6746-6758. |
| [6] | Jeong, H.M.;Lee, J.W.;Shin, W.H.;Choi, Y.J.;Shin, H.J.;Kang, J.K.;Choi, J.W..Nitrogen-doped graphene for high-performance ultracapacitors and the importance of nitrogen-doped sites at basal planes[J].Nano letters,20116(6):2472-2477. |
| [7] | Wenbo Lu;Xiaoyun Qin;Sen Liu;Guohui Chang;Yingwei Zhang;Yonglan Luo;Abdullah M. Asiri;Abdulrahman O. Al-Youbi;Xuping Sun.Economical, Green Synthesis of Fluorescent Carbon Nanoparticles and Their Use as Probes for Sensitive and Selective Detection of Mercury(II) Ions[J].Analytical chemistry,201212(12):5351-5357. |
| [8] | Yang, J.;Zhai, Y.;Deng, Y.;Gu, D.;Li, Q.;Wu, Q.;Huang, Y.;Tu, B.;Zhao, D..Direct triblock-copolymer-templating synthesis of ordered nitrogen-containing mesoporous polymers[J].Journal of Colloid and Interface Science,20102(2):579-585. |
| [9] | Zhongli Wang;Xinbo Zhang;Xiaojuan Liu.Co-gelation synthesis of porous graphitic carbons with high surface area and their applications[J].Carbon: An International Journal Sponsored by the American Carbon Society,20111(1):161-169. |
| [10] | Lim, S;Yoon, SH;Mochida, I;Jung, DH.Direct Synthesis and Structural Analysis of Nitrogen-Doped Carbon Nanofibers[J].Langmuir: The ACS Journal of Surfaces and Colloids,200914(14):8268-8273. |
| [11] | Hyun Chul Choi;Young Mee Jung;Isao Noda;Seung Bin Kim.A Study of the Mechanism of the Electrochemical Reaction of Lithium with CoO by Two-Dimensional Soft X-ray Absorption Spectroscopy (2D XAS), 2D Raman, and 2D Heterospectral XAS-Raman Correlation Analysis[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,200324(24):5806-5811. |
| [12] | Niiantha P. Wickramaratne;Vindya S. Perera;Byung-Wook Park.Graphitic Mesoporous Carbons with Embedded Prussian Blue-Derived Iron Oxide Nanoparticles Synthesized by Soft Templating and Low-Temperature Graphitization[J].Chemistry of Materials: A Publication of the American Chemistry Society,201314(14):2803-2811. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%