采用阳极氧化法在含氟的乙二醇溶液中以低碳钢为基体制备出高度有序排列的纳米管阵列结构氧化铁薄膜，并采用 SEM分析制备工艺参数对薄膜形貌和尺寸的影响；采用 XRD 和 XPS 对热处理前后薄膜表征.结果表明阳极氧化电压和氟离子浓度是影响薄膜形貌和纳米管尺寸最重要因素，在30~60 V 阳极氧化电压和0．03~0．1 mol/L NH4F范围内可以制备出管状结构的薄膜，且随阳极氧化电压升高，管径增加；随氟离子含量提高，管径增加.温度只是影响管状结构生长速度.经过500℃氩气气氛热处理后非晶态薄膜转化为主要由赤铁矿和少量磁铁矿构成的晶态薄膜.最后提出了纳米管形成机理.
Thin films consisting of highly self-organized nanotube arrays were fabricated on carbon steel substrate in an a-queous ethylene glycol solution containing fluoride by anodization.It has been investigated by SEM that several synthesis parameters,such as anodizing voltage,anodizing time,concentration of fluoride ion and temperature affected on the morphology of the film comprising nanotube arrays and tube size.XRD and XPS techniques have been used to character-ize the nanotube arrays film.Results show that anodization voltage and concentration of fluoride ion are the key factors to effect on the morphology of the film and tube size.The nanotube structured film forms between 30 and 60 V,and in the range of 0.03 and 0.1 mol/L NH4F.The average pore diameter of the tubes increases with the increases of the anodiza-tion voltage and concentration of fluoride ion.Temperature only has an influence on the rate of tube formation of flim. Amorphous film transforms into the crystallized film composed of predominant hematite phase and minor magnetite phase.Finally,the possible growth of nanotube arrays was also proposed.
参考文献
| [1] | 高家诚;王强;高正源.机械研磨金属表面纳米化的研究进展[J].功能材料,2010(5):741-745,750. |
| [2] | SteelSunny Sethi;Ali Dhinojwala.Superhydrophobic Conductive Carbon Nanotube Coatings for Steel[J].Langmuir: The ACS Journal of Surfaces and Colloids,20098(8):4311-4313. |
| [3] | Wang ZB.;Tao NR.;Li S.;Wang W.;Liu G.;Luc J.;Lu K..Effect of surface nanocrystallization on friction and wear properties in low carbon steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20031/2(1/2):144-149. |
| [4] | Wang ZB;Lu J;Lu K.Wear and corrosion properties of a low carbon steel processed by means of SMAT followed by lower temperature chromizing treatment[J].Surface & Coatings Technology,20066(6):2796-2801. |
| [5] | Basak, A.K.;Celis, J.-P.;Ponthiaux, P.;Wenger, F.;Vardavoulias, M.;Matteazzi, P..Effect of nanostructuring and Al alloying on corrosion behaviour of thermal sprayed WC-Co coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:377-385. |
| [6] | F. Fernandes;A. Ramalho;A. Loureiro;J. M. Guilemany;M. Torrell;A. Cavaleiro.Influence of nanostructured ZrO_2 additions on the wear resistance of Ni-based alloy coatings deposited by APS process[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):591-601. |
| [7] | Bagherzadeh, M.R.;Daneshvar, A.;Shariatpanahi, H..Novel water-based nanosiloxane epoxy coating for corrosion protection of carbon steel[J].Surface & Coatings Technology,20128/9(8/9):2057-2063. |
| [8] | Rangaraju, R.R.;Raja, K.S.;Panday, A.;Misra, M..Low-cost photoelectrocatalyst based on a nanoporous oxide layer of low-carbon steel[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,201044(44):445301-1-445301-8. |
| [9] | Chih-Yung Chang;Chih-Hao Wang;Chung-Jen Tseng;Kong-Wei Cheng;Lih-Wu Hourng;Bin-Tsang Tsai.Self-oriented iron oxide nanorod array thin film for photoelectrochemical hydrogen production[J].International journal of hydrogen energy,201218(18):13616-13622. |
| [10] | Haripriya E Prakasam;Oomman K Varghese;Maggie Paulose.Synthesis and photoelectrochemical properties of nanoporous Iron (III) oxide by potentiostatic anodization[J].Nanotechnology,200617(17):4285-4291. |
| [11] | Raghu R. Rangaraju;K. S. Raja;A. Panday;M. Misra.An investigation on room temperature synthesis of vertically oriented arrays of iron oxide nanotubes by anodization of iron[J].Electrochimica Acta,20103(3):785-793. |
| [12] | Susanta K. Mohapatra;Shiny E. John;Subarna Banerjee.Water Photooxidation by Smooth and Ultrathin α-Fe_2O_3 Nanotube Arrays[J].Chemistry of Materials: A Publication of the American Chemistry Society,200914(14):3048-3055. |
| [13] | Aiming Mao;Kahee Shin;Jung Kyu Kim.Controlled Synthesis of Vertically Aligned Hematite on Conducting Substrate for Photoelectrochemical Cells: Nanorods versus Nanotubes[J].ACS applied materials & interfaces,20116(6):1852-1858. |
| [14] | Xie, K.;Li, J.;Lai, Y.;Lu, W.;Zhang, Z.;Liu, Y.;Zhou, L.;Huang, H..Highly ordered iron oxide nanotube arrays as electrodes for electrochemical energy storage[J].Electrochemistry communications,20116(6):657-660. |
| [15] | Zhonghai Zhang;Md. Faruk Hossain;Takakazu Takahashi.Self-assembled hematite (α-Fe2O3) nanotube arrays for photoelectrocatalytic degradation of azo dye under simulated solar light irradiation[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,20103/4(3/4):423-429. |
| [16] | Thomas J. LaTempa;Xinjian Feng;Maggie Paulose.Temperature-Dependent Growth of Self-Assembled Hematite (a-Fe2O3) Nanotube Arrays: Rapid Electrochemical Synthesis and Photoelectrochemical Properties[J].The journal of physical chemistry, C. Nanomaterials and interfaces,200936(36):16293-16298. |
| [17] | Deng, Hongda;Huang, Mao-Chia;Weng, Wei-Heng;Lin, Jing-Chie.Photocathodic protection of iron oxide nanotube arrays fabricated on carbon steel[J].Surface & Coatings Technology,2015:183-187. |
| [18] | Burleigh TD;Dotson TC;Dotson KT;Gabay SJ;Sloan TB;Ferrell SG.Anodizing steel in KOH and NaOH solutions[J].Journal of the Electrochemical Society,200710(10):C579-C586. |
| [19] | Room temperature formation of half-metallic Fe_(3)O_(4) thin films for the application of spintronic devices[J].Applied physics letters,20038(8):1590-1592. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%