研究了动应力(往复弯曲疲劳应力)对氯化物溶液中不锈钢点蚀敏感性的促进作用.在固溶态316L不锈钢表面点蚀孔中产生了明显的非敏化态晶间腐蚀.在点蚀孔内受腐蚀晶界处孕育产生了初态腐蚀疲劳裂纹,裂纹由沿晶转变为穿晶扩展,形成主裂纹并继续扩展直至材料失稳断裂.阐述了在动应力和侵蚀性介质联合作用下CF裂纹萌生的过程机理.论述了动应力-环境介质-材料特性在多种腐蚀类型交互作用中的贡献和相关性.
参考文献
[1] | Parkings R N. Environment-Induced Cracking of Metals, eds, Gangloff R P,Ives M B Houston, TX:NACE,1990,1 |
[2] | Cottis R A, Husain Z. Metals Technology, 1982, 9:104 |
[3] | Leis B N, Rungta R, Mayfield M E, Beavers J A. "Corrosion Fatigue Crack Initiation in an Iron-Caustic System", in Corrosion Fatigue: Mechanics, Metallurgy, Electrochemistry and Engineering, eds. Crooker T W , Leis B N, ASTM STP 801, Philadelphia, PA: ASTM 1983: 197 |
[4] | Srivatsan T S, Sudarshan T S. J. Mater. Sci. 1988, 23(1):521 |
[5] | Husain Z, Mater. Sci. Eng. A., 1989, A119: L1 |
[6] | Goto M, Nisitani H. Fat. Fract. Eng. Mater. Struct., 1992, 5:353 |
[7] | Speckhardt H. "Study of the Superposition of Intergranular Corrosion and Pitting Corrosion by Fatigue Cracking of Stainless Steels", in Corrosion Fatigue: Chemistry, Mechanics, and Microstructure, eds. Devereus O F, McEvily A J, Staehle R W, NACE-2, Houston, TX: NACE 1972:557 |
[8] | Kiessling R. Nonmetallic Inclusions in Steel, London, The Metal Society, 1988 |
[9] | Shih T Y, Araki T. Trans. Iron. Steel. Inst. Jap., 1973, 13: 11 |
[10] | Payer J H, Staehle R W. "Mechanisms of Fatigue Crack Nucleation", in Corrosion Fatigue: Chemistry, Mechanics, and Microstructure, eds. Devereux O F, McEvily A J, Staehle R W, NACE-2, Houston, TX: NACE 1972: 211 |
[11] | Shalaby H M, Begley J A, Macdonald D D. Corrosion, 1996, 52: 262 |
[12] | Pakings R N. Metals Technology, 1982, 9: 122 |
[13] | Laird C, Duguette D J. "Mechanismus of Fatigue Crack Nucleation", in Corrosion Fatigue: Chemistry, Mechanics, and Microstructure, eds. Devereux O F, McEvily A J, Staehle R W, NACE-2, Houston TX: NACE 1972: 88 |
[14] | 王永智,腐蚀科学与防护技术,1996, 8:1 |
[15] | Wang Y, Akid R, Corrosion, 1996, 52: 92 |
[16] | Evans U R, The Corrosion and Oxidation of Metals, London, Edward Arnold, 1960 |
[17] | Qian Y R, Cahoon J R, Corrosion, 1997, 53: 129 |
[18] | Iman M R, Fraker A C, Gilmore C M, Corrosion and Degradation of Implant Materials, ASTM STP 684, 1979, 128 |
[19] | 谢建辉.博士论文,北京科技大学,1997 |
[20] | 谢建辉,吴荫顺,朱日彰.中国腐蚀与防护学报,1997, 17(1): 31 |
[21] | 谢建辉,吴荫顺,朱日彰.金属学报,1997,33(3): 304 |
[22] | 谢建辉,吴荫顺,朱日彰.中国生物医学工程学报,1997, 16(3): 277 |
[23] | Xie J H, Wu Y S, et al. ACTA Metallurgica Sinica, 1996, 9(5): 333 |
[24] | Armijo J S, Corrosion, 1968, 24(1): 24 |
[25] | Armijo J S, Wilde B E, Corrosion Science, 1968, 8: 649 |
[26] | 王月平,于福洲.中国腐蚀与防护学报,1988, 8(2): 86 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%