利用CHI630电化学分析测试仪测试了在浸锌溶液中加入不同表面活性剂及加入不同含量的最优表面活性剂后试片活化电位随浸锌时间的变化曲线和浸锌后的试片在3.5%NaCl溶液中的极化曲线,对其耐蚀性能进行了研究.结果表明,表面活性剂可以提高浸锌后试片的稳定电位,提高浸锌层在3.5%NaCl溶液中的耐蚀性;并确定了表面活性剂A是较适宜的浸锌溶液中的表面活性剂,其最佳用量为0.1 g/L-0.15 g/L.同时,利用SEM、EDS对浸锌层、断面、镀镍层的形貌和成分进行了分析.镀层结合力合格.
参考文献
| [1] | 弗利德里克著.北京航空学院译.现代电镀[M].北京:机械工业出版社,1974.712. |
| [2] | S G Robertson,I M Ritchie.The role of iron(Ⅲ) and tartrate in the zincate immersion process for plating aluminium[J].Jovrnal of Applied Electrochemistry,1997.27:799. |
| [3] | F J Monteiro.Surfece Engineering[J].Surface and Interface Analysis,1990,6(4):287. |
| [4] | F J Monteiro,M A Barbosa.Pretreatments to improve the adhesion of electrode posits on aluminium[J].Surface and Interface Analysis,1991,17(7):519. |
| [5] | Williams,Barry.Gyanide containing pretreatment processes for plating on alu minum and its alloys:Are they really necessary?[J].Proceeadings of the AESF An nual Technical Conference,1999,24:533. |
| [6] | T Pearson,S Wake.Verbesserungen bei der Vorbehandlung von Aluminium als Sub straffuerdie galvanische Abscheidung[J].Galvanotechnik,2000,91(11):3054. |
| [7] | Anon.Trevorpearson of Improvments in the pretreatment of Aluminum as asubst rute for Electrodeposition[J].Trans,IMF,1997,75(3):25. |
| [8] | A K Sharma,H Bhojaraj.Electroless nickel and gold plating on titanium alloy s for space applications[J].Metal Finishing,1992,90(7):23. |
| [9] | 邱文革,陈树森.表面活性剂在金属加工中的应用[M].北京:化学工业出版社,2003,12 3. |
| [10] | 李宁,屠振密.化学镀实用技术[M].北京:化学工业出版社.2004.250. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%