以紧固孔结构件腐蚀疲劳试验为基础,研究了腐蚀疲劳裂纹虚拟扩展方法即随机过程和AFGROW模拟方法.以试验数据拟合得到的Paris公式为基础,在随机过程方法中考虑了正态随机过程和对数正态随机过程,得到裂纹长度和循环数之间的模拟曲线,给出指定循环数下裂纹长度的概率模型并和实验结果进行了比较.利用AFGROW对腐蚀疲劳裂纹扩展进行了模拟,裂纹扩展模拟曲线与实验值符合较好.
参考文献
| [1] | Wu W F,Ni CC.A study of stochastic fatigue crack growth modeling through experimental data[J].Probebilistic Engineering Mechanics,2003,18(1):107. |
| [2] | Maymon G.Virtual Crack Propagation Tests with application to probability of failure estimation[C].AIAA 2003-1992.44th AIAA/ASME/ASCE/AHs structures,structural dynmics,and materials confere 7-10 April 2003,Norfolk,Virginia. |
| [3] | Maymon G.Probabilistic crack growth behavior of aluminum 2024-T351 alloy using the'unified'approach[J].International Journal of Fatigue,2005,27(7):828. |
| [4] | 张有宏.飞机结构的腐蚀损伤及其对寿命的影响[D].西安:西北工业大学,2007.3. |
| [5] | Bellinger N C,Komorowski J P,Benak T J.Residual life predictions of corroded fuselage lap joints[J].International Journal of Fatigue,2001,23(1):S349. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%