利用阳极极化曲线法、Tafel曲线法和电化学阻抗谱法等技术,研究含有各种模拟热稳定性盐(HSS)的N-甲基二乙醇胺(MDEA)溶液在含氧与除氧条件下以及不同温度下对碳钢的腐蚀行为.结果表明,HSS的存在使碳钢的腐蚀速度加快.常温下HSS中的Cl-对碳钢的腐蚀性最强、可导致碳钢发生孔蚀;溶解氧的存在有利于降低既定HSS的腐蚀性.温度升高,碳钢的全面腐蚀速度增加,宏观孔蚀受到抑制;在含HSS的MDEA溶液中,碳钢腐蚀反应的阴极过程为电化学反应和扩散传质混合控制,阳极过程为电化学反应控制.
参考文献
| [1] | 叶庆国,张书圣.酸性废气脱硫工艺中N-甲基二乙醇胺降解反应产物的研究[J].高校化学工程学报,2001,15(1):35. |
| [2] | Cummings A L,Mecum S M.Remove heat stable salts for better amine plantt performance[J].Hydrocarbon Process.,1998,77(8):63. |
| [3] | Guo X-P,Tomoe Y.The effect of corrosion product layers on the anodic and cathodic reactions of carbon steel in CO2-saturated MDEA solutions at 100℃[J].Corrosion Science,1999,41:1391. |
| [4] | Cummings A L,Veatch F C,Keller A E.Corrosion and corrosion control methods in amine systems containing hydrogen sulfide[J].Chemical Treatment,1998,(1):42. |
| [5] | Rooney P C,Bacon T R,DuPart M S.Effect of heat stable salts on MDEA solution corrosivity[J].Hydrocarbon Process.,1996,75(3):95. |
| [6] | Winyu T,Amomvedee V,Bryce M G.Electrochemical investigation on the effect of heat-stable salts on corrosion in CO2 capture plants using aqueous solution of MEA[J].Ind.Eng.Chem.Res,2006,45 (8):2586. |
| [7] | 罗芳.胺法气体脱硫胺液中热稳态盐离子的组成分析[J].石油炼制与化工,2005,36(3):60. |
| [8] | 曹楚南.腐蚀电化学原理(第二版)[M].北京:化学工业出版社,2004.22,259,283. |
| [9] | 中国腐蚀与防护学会.金属的局部腐蚀[M].北京:化学工业出版社,1995.15,59. |
| [10] | 杨怀玉,陈家坚,曹楚南,等.H2S水溶液中的腐蚀与缓蚀作用机理的研究-Ⅳ[J].中国腐蚀与防护学报,2000,20(5):287. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%