采用动电位极化和交流阻抗技术研究了NS4溶液中的溶解氧对X80管线钢在该溶液中耐蚀性的影响,通过SEM、XRD等对X80管线钢的腐蚀形貌和腐蚀产物进行了分析.结果表明,随着NS4溶液中溶解氧含量的减少,X80钢的腐蚀电位升高,腐蚀电流密度降低,腐蚀产物的致密性逐渐提高,X80钢的耐蚀性增加;氧含量较高时,腐蚀产物表面高低不平,表面存在大量裂缝、孔洞等缺陷,表面致密性较差,氧含量减少后,腐蚀产物平整致密;随着溶解氧含量的不同,腐蚀后生成了不同的腐蚀产物.
参考文献
| [1] | 庄传晶,冯耀荣,霍春勇,等.国内 X80 级管线钢的发展及今后的研究方向[J].焊管,2005,28(2):10. |
| [2] | 方丙炎,王俭秋,朱自勇,等.埋地管道在近中性pH和高pH环境中的应力腐蚀破裂[J].金属学报,2001,37(5):453. |
| [3] | Lu B T,Luo J L.Relationship between yield strength and near-neutral pH stress corrosion cracking resistance of pipeline steels-an effect of microstructure[J].Corrosion,2006,62(2):129. |
| [4] | Chen W,King F,Vokes E.Characteristics of near-neutral-pH Stress corrosion cracks in an X-65 pipeline[J].Corrosion,2002,58(3):267. |
| [5] | Parkins R N,Blanchard Jr W K,Delanty B.Transgranular stress corrosion cracking of high-pressure pipelines in contact with solutions of near neutral pH[J].Corrosion,1994,50(5):394. |
| [6] | Chen W,King F,Jack T R,et al.Environmental aspects of near-neutral pH stress corrosion cracking of pipeline steels[J].Metallurgical and Materials Transactions A,2002,33A(5):1429. |
| [7] | Wang S H,Chen W,King F,et al.Preeyclic-loading-induced stress corrosion cracking of pipeline steels in a near-neutral pH soil environment[J].Corrosion,2002,58(6):526. |
| [8] | 杨熙珍,杨武.金属腐蚀电化学热力学[M].北京:化学工业出版社,1991.25. |
| [9] | 李谋成.林海潮,曹楚南.碳钢在土壤中腐蚀电化学阻抗谱特征[J].中国腐蚀与防护学报,2000,20(2):111. |
| [10] | Manfredi C,Otegui J L.Failure by SCC in buried pipelines[J].Engineering Failure Analysis,2002,9:495. |
| [11] | 李伟善,蔡松琦.Fe/硼酸盐缓冲溶液界面性质的交流阻抗研究[J].华南师范大学学报(自然科学版),2003,(3):80. |
| [12] | Sarin P,Snoeyink V L Bebee J,et al.Iron release from corroded iron pipes in drinking water distribution systems:effect of dis-solved oxygen[J].Water Research,2004,38(5):1259. |
| [13] | Mclntire G,Lippert J,Yudelson J.The effect of dissolved CO2 and O2 on the corrosion of iron[J].Corrosion,1990,46(2):91. |
| [14] | Park J J,Pyun S I,Na K H,et al.Effect of passivity of the oxide film on low-pH strees corrosion cracking of API 5L X-65 pipe-line steel in bicarbonate solution[J].Corroaion,2002,58(4):329. |
| [15] | He D X,Chen W,Luo J L.Effect of cathodic potential on hy-drogen content in a pipeline steel exposed to NS4 vear-veutral pH soil solution[J].Corrosion,2004,60(8):778. |