苎麻纤维经改性降低极性及吸水率后与聚丙烯复合后可作为新型的优良汽车内饰件材料.实验发现,三聚氰胺甲醛树脂可降低苎麻纤维的吸水率,但三聚氰胺甲醛树脂存放稳定性差,加入聚乙烯醇进行改性可显著改善三聚氰胺甲醛树脂的贮存稳定性.研究聚乙烯醇加入量、反应终点、反应温度、pH值及其调整方式、反应结束后溶液pH值的调整温度对溶液贮存稳定性的影响.得到可稳定贮存2个月的聚乙烯醇改性三聚氰胺甲醛树脂.使用自制的三聚氰胺甲醛树脂对苎麻进行改性处理,测试改性前后的吸水率,苎麻纤维经三聚氰胺甲醛树脂改性后吸水率显著降低.
参考文献
| [1] | Hua L;Zadorecki P;Fledin P .Cellulose Fiber-polyester Composites with Reduced Water Sensitivity.1:Chemical Treatment and Mechanical Properties[J].Polymer Composites,1987,8(03):199. |
| [2] | Hua L;Flodin P;R(o)nnhult T .Cellulose Fiber-polyester Composites with Reduced Water Sensitivity.2:Surface Analysis[J].Polymer Composites,1987,8(03):203. |
| [3] | Shukla S R;Rao G V et al.Improving graft level during photo induced graft copolymerization of styrene onto cotton cellulose[J].Journal of Applied Polymer Science,1993,49(08):1423-1430. |
| [4] | Semsarzadeh M A;Lotfali A R.Mirradeh脂复合材料研究[J].玻璃钢/复合材料,1997(03):12-14. |
| [5] | Jute reinforced polyester structures[J].Polymer Composites,1984,5(02):141-142. |
| [6] | 杨桂成;曾汉民;李家驹.剑麻纤维/酚醛树[M]. |
| [7] | 曾竟成,肖加余,梁重云,张长安,张纯禹.黄麻纤维增强聚合物复合材料工艺与性能研究[J].玻璃钢/复合材料,2001(02):30-33. |
| [8] | 唐星华.木材用胶粘剂[M].北京:化学工业出版社,2002 |
| [9] | Ю.Г.多罗宁;等;李庆章.木材工业用合成树脂[M].北京:中国林业出版社,1984 |
| [10] | 张立芳.合成树脂饰面人造板[M].北京:化学工业出版社,2004 |
| [11] | 于夺福.装饰板制造与应用[M].北京:中国林业出版社,1983 |
| [12] | 张海滨;陈新生.低压短周期饰面用三聚氰胺甲醛树脂的开发[J].建筑人造板,1999(02):26-27. |
| [13] | 余兴华.解决聚乙烯醇缩甲醛水性胶质量问题的方法[J].安徽科技,1997(01):48-51. |
| [14] | 李东光.脲醛树脂胶粘剂[M].北京:化学工业出版社,2004 |
| [15] | 张长安,鲁博,曾竟成,张一甫.苎麻落麻的表面处理及其复合材料的性能研究[J].工程塑料应用,2004(11):5-9. |
| [16] | 《涂料工艺》编委会.涂料工艺(第三版上册)[M].北京:化学工业出版社,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%