为了将太湖淤泥用作片状模塑料复合材料的填料,从淤泥物化性能和结构特征对太湖淤泥进行了表征和分析.对太湖淤泥分别采用XRF分析化学成分,XRD分析矿物成分,颗粒分析仪分析粒径分布,SEM观察淤泥的微观形貌,IR和NMR分析淤泥的结构特征,并分析淤泥的吸油值.结果表明,淤泥的化学成分和矿物组成适合于成为片状模塑料硅酸盐类填料,淤泥的中位径(D50)与片状模塑料的碳酸钙填料近似,淤泥含有有机基团的特征更适宜与片状模塑料树脂均匀结合,并导致其吸油值高于碳酸钙填料.太湖淤泥作为再生资源可用于片状模塑料填料.
The possibility of Taihu Lake silt applied for the sheet molding compound filler was studied from the silt chemical and physical properties and its structure. XRF was used to analyze the chemical compositions, the mineral phases was analyzed by XRD, the particle size distribution was detected by photo size analyzer, SEM was used to observe the morphology of the silt, the structural specialties of the silt were characterized by IR and NMR, and the oil-absorbing value of the silt was also measured. These analyzed results showed that the chemical composition and mineral composition of the silt was suitable for a silicate filler of sheet molding compound. The D50 of Taihu Lake silt was similar to the calcium carbonate filler of sheet molding compound, and the organic groups of the silt contained made it easily combine homogenously with sheet molding compound resin, which also had a higher oil-absorbing value than the calcium carbonate. The Taihu Lake silt was suitable for sheet molding compound filler according to its up characters.
参考文献
| [1] | 顾欢达,顾熙.河道淤泥的有效利用方式及其物性探讨[J].环境科学学报,2002(04):454-458. |
| [2] | 李志威,朱书景.改性淤泥做码头填筑材料试验研究[J].水运工程,2006(06):85-88. |
| [3] | Kunio Minegishi;Katsuhiko Makiuchi;Paiki Takahashi.Strength-deformational characteristic of EPS beads-mixed lightweight geomaterial subjected to cyclic loading.Proceedings of the International Workshop on Lightweight Geo-materiels[A].,2002:119-124. |
| [4] | Zoubeir Lafhaj;Mazen Samara;Franck Agostini.Polluted river sediments from the North region of France:Treatment with Novosol process and valorization in clay bricks[J].Construction and Building Materials,2008(22):755-762. |
| [5] | 于漧.江河湖海淤泥资源化及其在烧砖中的应用[J].砖瓦,2007(02):21-24. |
| [6] | K.Hamer;V.Karius .Brick production with dredged harbour zediments.An industrial-scele experiment[J].WASTE MANAGEMENT,2002,5(22):521-530. |
| [7] | V.Karins;K.Hamer .pH and grain-size variation in leaching tests with bricks made of barbour sediments compared to commercial bricks[J].Science of the Total Environment,2001,3(278):73-85. |
| [8] | Chih-Huang Weng;Deng-Fong Lin;Pen-Chi Chiang .Utilization of sludge as brick materials[J].Advances in environmental research,2003(3):679-685. |
| [9] | 范锦忠.利用淤泥生产人造轻骨料--陶粒[J].砖瓦,2007(11):59-62. |
| [10] | 刘雄亚;谢怀勤.复合材料工艺及设备[M].武汉:武汉理工大学出版社,2006:82-89. |
| [11] | 李忠恒,张宁,陶国良.SBS改性SMC复合材料的研究[J].玻璃钢/复合材料,2007(04):34-37. |
| [12] | Jue Lu;Shrikant Khot;Richard P.Wool .New sheet molding compound resins from soybean oil.I.Synthesis and characterization[J].Polymer: The International Journal for the Science and Technology of Polymers,2005(1):71-80. |
| [13] | 冯增申,邹宇知.SMC树脂及其质量控制技术[J].玻璃钢/复合材料,2000(02):26-27. |
| [14] | 杨南如.无机非金属材料测试方法[M].武汉:武汉理工大学出版社,2005:259. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%