C和V对奥氏体不锈钢焊缝的强化

1.哈尔滨工业大学,黑龙江,哈尔滨,150001;洛阳船舶材料研究所,河南,洛阳,471039

2.哈尔滨工业大学,黑龙江,哈尔滨,150001

3.哈尔滨工业大学,黑龙江,哈尔滨,150001

4.洛阳船舶材料研究所,河南,洛阳,471039

5.洛阳船舶材料研究所,河南,洛阳,471039

Strengthening Effect of C and V on Austenite Stainless Steel Welds

研究了元素C、V对高强度奥氏体不锈钢焊缝金属的强化作用.结果显示,提高C含量,具有明显的固溶强化效果,但C含量的增加导致大量碳化物在晶界上析出;提高V含量使细小弥散的碳化钒在晶内析出,产生明显的沉淀强化效果.在强化效果基本相同时,后者的韧性高于前者.

[1]	Murti V S R;Sastry Y R;Rao V GN et al.Some studies on the service weldability of HSLA steels using 18Cr,8Ni,6Mn type austenitic electrodes[J].Journal of Materials Processing Technology,1993,37:759-765.
[2]	Uggowitzer P J;Harzenmoser M.氮对奥氏体不锈钢的强化效应[A].上海:上海钢铁研究所,1990:120-125.
[3]	M.D.C. Sobral;P.R. Mei;H.-J. Kestenbach .Effect of carbonitride particles formed in austenite on the strength of microalloyed steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):317-321.
[4]	Y. Yazawa;T. Furuhara;T. Maki .Effect of matrix recrystallization on morphology, crystallography andcoarsening behavior of Vanadium carbide in austenite[J].Acta materialia,2004(12):3727-3736.
[5]	Frisk K;Hillert M.氮在钢中的某些有益作用[A].上海:上海钢铁研究所,1990:1-21.
[6]	Erich Folkhard;栗卓新;朱学军.不锈钢焊接冶金[M].北京:化学工业出版社,2004

上一张下一张

计量

作者相关

文章评分