分析了目前乙烯裂解装置中产生结焦现象的原因,鉴于涂层技术在乙烯裂解装置抗结焦应用中的优势,重点介绍了涂层技术在抗结焦中应用的研究进展,并提出了该技术在乙烯裂解装置中实现工业化的建议.
参考文献
| [1] | Boehm H P .Carbon from carbon monoxide disproportion on nickel and iron catalyst:morpholcgical studies and possible growth mechanisms[J].CARBON,1973,11:583-590. |
| [2] | Jackson P R S;Young D J;Trimm D L .Coke deposition on and removal from metals and heat-resistant alloys understeamcracking conditions[J].Journal of Materials Science,1986,21:4376-4384. |
| [3] | Jackson P R S;Trimm D L;Young D J .The coking kinetic of heat resistant austenitic steels in hydrogenpropylene atmosphere s[J].Journal of Materials Science,1986,21:3125-3134. |
| [4] | Lahaye J;Baide P;Ductet J .Mechanism of carbon formation during steamcracking of hydrocarbon[J].Carbon,1977,15:87-93. |
| [5] | Baker R T K;Yates D J C;Dumesic J A.Mechanism of carbon fomation during steamcracking of hydrocarbon[M].New York,1981 |
| [6] | Alstrup I .A new model explaining carbon filament growth on nickel,iron and Ni-Cu alloy catalysts[J].Journal of Catalysis,1988,109:247-251. |
| [7] | Baker R T K .Catalytic growth of carbon filaments[J].Carbon,1989,27(03):315-323. |
| [8] | Snoeck JW.;Fowles M.;Froment GF. .FILAMENTOUS CARBON FORMATION AND GASIFICATION - THERMODYNAMICS, DRIVING FORCE, NUCLEATION, AND STEADY-STATE GROWTH[J].Journal of Catalysis,1997(1):240-249. |
| [9] | Snoeck JW.;Fowles M.;Froment GF. .KINETIC STUDY OF THE CARBON FILAMENT FORMATION BY METHANE CRACKING ON A NICKEL CATALYST[J].Journal of Catalysis,1997(1):250-262. |
| [10] | 江林.乙烯裂解炉结焦抑制技术进展[J].当代石油石化,2003(03):35-38. |
| [11] | 李处森,于力,杨院生.三种金属及其氧化物膜在碳氢化合物热裂解反应中结焦行为的研究[J].中国腐蚀与防护学报,2001(03):158-166. |
| [12] | 李处森,杨院生.金属材料在高温碳气氛中的结焦与渗碳行为[J].中国腐蚀与防护学报,2004(03):188-192. |
| [13] | 李处森,杨院生,吴欣强.HP耐热钢结焦、渗碳的原因分析[J].中国腐蚀与防护学报,2002(05):286-289. |
| [14] | Li CS;Yang YS .A glass based coating for enhancing anti-coking and anti-carburizing abilities of heat-resistant steel HP[J].Surface & Coatings Technology,2004(1):68-73. |
| [15] | 樊黑钦,崔德春,李锐.裂解炉管涂层材料的制备及其作用机理的研究[J].乙烯工业,2003(01):26-29. |
| [16] | Kim A Wynns;George T Bayer .Diffusion coated ethylene furnace Tubes[P].US 5873951,1999. |
| [17] | Kim A Wynns .Diffusion method for coating high temperature nickel chromium[P].US 6139649,2000. |
| [18] | Young D J .Alcroplex technics of alon surface technology[J].European Chemical News,1998,69(1822):27. |
| [19] | Kukes Semyon et al.Method for reducing carbon formation in a thermal cracking process[P].US 4410418,1983. |
| [20] | Petrone S S A;Oballa M C et al.Surface on a stainless steel matrix[P].CA 2355436Al,2002. |
| [21] | Perrone S S A;Mandyam R C et al.Surface alloyed high temperature alloys[P].US 6093260,2000. |
| [22] | Fisher G A;Prescott T et al.Coating system for high temparature stainless steel[P].US 6585864,2003. |
| [23] | Takeuchi Yuko;Kato Yoshihisa et al.Multilayered anti-coking heatResistant metal tube and method for manufacture thereof[P].US 6579628,2003. |
| [24] | Cheol K S;Seop C A;Hyun C D et al.Method of on-line coating film on the inner walls of the reaction tubes in a hydrocarbon pyrolysis reactor[P].US 6514563,2003. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%