在大气和大气与SO2气体混合污染条件下研究了NaCl对Mg-Al-Ca合金腐蚀情况的影响,讨论了镁合金腐蚀动力学、腐蚀产物及微观组织腐蚀形貌的变化情况.NaCl在大气中生成的腐蚀产物起到了一定的保护作用,导致腐蚀速率降低.在SO2环境中,生成的腐蚀产物不具有阻碍腐蚀的作用,大量难溶物在镁合金表面难以短时间形成,故NaCl和SO2同时存在引起的腐蚀远大于NaCl单一因素存在时引起的腐蚀.
参考文献
| [1] | Qing QU,Chuanwei YAN,Lei ZHANG,Ye WAN,Chunan CAO.Influence of NaCl Deposition on Atmospheric Corrosion of A3 Steel[J].材料科学技术学报(英文版),2002(06):552-555. |
| [2] | 刘正;张奎;曾小勤;著.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002:54-59. |
| [3] | Falk T;Svesson J E;Johansson L G .The influence of CO2 and NaCl in the atmospheric corrosion of zinc[J].Journal of the Electrochemical Society,1998,145(09):2993. |
| [4] | Lindstrom R;Svensson J E;Johansson LG .The influence of carbon dioxide in the atmospheric corrosion of some magnesium alloys in the presence of NaCl[J].Journal of the Electrochemical Society,2002,149(04):B103. |
| [5] | 林翠,李晓刚.NaCl沉积和SO2污染对镁合金初期大气腐蚀行为的影响[J].北京科技大学学报,2004(05):524-528. |
| [6] | Guangling Song;Aanrej Atrens;Matthew Dargusch .Influence of mcrostructure on the crrosion of de-cast AZ91D[J].Corrosion Science,1999,41(02):249-73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%