运用极化曲线、循环极化曲线等电化学方法研究了OCr17Ni4Cu4Nb钢经不同工艺固溶处理后的耐海水腐蚀性能,并对显微组织进行了观察和分析.试验结果表明:在1040℃下该不锈钢经60min固溶处理可获最佳的耐海水腐蚀性能和较高的硬度值.其显微组织主要为淬火马氏体+少量的残余奥氏体+δ-铁素体,且晶粒大小均匀.
参考文献
| [1] | Sergio S.M. Tavares;Juan Manuel Pardal;Joaquim S. Corte .Failure induced by severe wear between studs and nuts of 17-4PH steel[J].Engineering failure analysis,2009(5):1765-1769. |
| [2] | Liu R L;Yan M F .Improvement of wear and corrosion resistances of 17-4PH stainless steel by plasma nitrocarburizing[J].Materials & Design,2010,31:2355-2359. |
| [3] | 马力,阎永贵,李小亚.时效处理对CrCoMo不锈钢耐蚀性能的影响[J].腐蚀与防护,2004(09):376-378. |
| [4] | 赵莉萍,杨慧,李慧琴.固溶处理和时效对17-4PH沉淀硬化不锈钢组织性能的影响[J].特殊钢,2003(04):24-25. |
| [5] | 戚正风.固态金属中的扩散与相变[M].北京:机械工业出版社,1998:354-367. |
| [6] | Hsiao CN.;Chiou CS.;Yang JR. .Aging reactions in a 17-4 PH stainless steel[J].Materials Chemistry and Physics,2002(2):134-142. |
| [7] | Viswanathan U K;Banerjee S;Krishnan R .Effects of aging on the microstructure of 17-4PH stainless steel[J].Materials Science and Engineering,1988,104(C):181-189. |
| [8] | 康煜平.金属固态相变及应用[M].北京:化学工业出版社,2007:92. |
| [9] | 沙维 .马氏体时效钢的析出产物[J].钢铁,1994,29(11):49-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%