用微乳液和碳吸附耦合法制备了氧化钐、氧化钆二元稀土掺杂氧化铈纳米粉体(Sm2O3)0.08(Gd2O3)0.02(CeO2-δ)0.8.探讨了碳黑的加入量对粉体表面积的影响,得到最佳的碳黑加入量.利用XRD、TEM和BET方法对其物相、分散性、颗粒形貌和比表面积等性能进行了表征.结果表明:700℃焙烧的粉体呈现良好的结晶状态,为立方萤石结构,比表面积为65m2/g ,平均颗粒直径为12nm,分散良好. 利用交流阻抗法测试了材料的电导率.结果表明,电导率随烧结温度的升高而增大.
参考文献
| [1] | Christopher Milliken;Sivaraman Guruswamy;Ashok Khandkar .Properties and Performance of Cation-Doped Ceria Electrolyte Materials in Solid Oxide Fuel Cell Applications[J].Journal of the American Ceramic Society,2002(10):2479-2486. |
| [2] | 刘莉,唐超群.CeO2基中低温固体电解质材料研究进展[J].电源技术,2001(06):428-431. |
| [3] | Inaba H.;Tagawa H. .CERIA-BASED SOLID ELECTROLYTES - REVIEW [Review][J].Solid state ionics,1996(1/2):1-16. |
| [4] | Steele BCH. .Appraisal of Ce1-yGdyO2-y/2 electrolytes for IT-SOFC operation at 500 degrees C[J].Solid state ionics,2000(1/4):95-110. |
| [5] | Yahiro H;Eguchi K;Arai H .Electrical properties and reducibilities of ceria-rare earth oxide system and their application to solid oxide fuel cell[J].Solid State Ionics,1989,36:71. |
| [6] | 贺拥军,杨伯伦.微乳液和均匀沉淀耦合法制备CeO2纳米粒子[J].化学通报,2003(02):120-124. |
| [7] | 范雄.金属X衍射学[M].北京:机械工业出版社,1998 |
| [8] | Paul C Hiemenz.胶体与表面化学原理[M].北京:北京大学出版社,1986 |
| [9] | Kim D J .Lattice parameters,ionic conductivities and solubility limits in fluorite-structure MO2 oxide (M=Hf4+,Zr4+,Ce4+,Th4+,U4+) solid solution[J].Journal of the American Ceramic Society,1989,72(08):1415-1421. |
| [10] | 李英,谢裕生,龚江宏,唐子龙,张中太.制备工艺对（ZrO2）0.90-（Y2O3）0.04-（CaO）0.06电解质材料电性能的影响[J].电源技术,2001(05):330-332,336. |
| [11] | 刘继进,何莉萍,陈宗璋,向兰翔,邵长贵,罗上庚.氧化钇掺杂四方氧化锆电性能的研究[J].硅酸盐学报,2003(03):241-245. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%