采用溶胶-凝胶法制备了钙钛矿型La1-xSrxMnO3和(La0.7Sr0.3)1-yKyMnO3粉体,研究了溶胶-凝胶法合成条件对样品的比饱和磁化强度的影响.利用XRD对样品结构进行表征,结果表明,Sr的掺入量不影响La1-xSrxMnO3结构,(La0.7Sr0.3)1-yKyMnO3系列样品由于K+的半径与La3+,Sr2+不匹配,掺杂浓度仅为0.01就已经出现杂相峰,超过0.1时杂峰增多.通过振动样品磁强计测试样品的磁性质,结果表明,x≤0.3的范围内La1-xSrxMnO3系列样品的比饱和磁化强度随着x的增加而增加,当x>0.3后随x的增加而减弱,(La0.7Sr0.3)1-yKyMnO3系列样品的比饱和磁化强度随Y的增加而下降.
参考文献
| [1] | Wang Z L;Kang Z C.Functionnal and smart materials[M].New York:Pleunm Press,1998:93-149. |
| [2] | Huang YH.;Yan CH.;Wang ZM.;Zhu T.;Liao CS.;Gao S.;Xu GX.;Xu ZG. .Soft chemical synthesis and transport properties of La0.7Sr0.3MnO3 granular perovskites[J].Solid State Communications,2000(1):43-47. |
| [3] | Songling Huaag;Xugao Cui;Dunhui Wang et al.Magnetic entrogy change and magetotransport in Gd doped La-Sr-Mn-O pervskite[J].Journal of Alloys and Compounds,2005,398(1-2):184-187. |
| [4] | Nicholas Gnmdy A;Bengt Hallstedt;Ludwig J Gauekler .La1-xMn1-yO3-x,perovsidtes modelled with and without antisite defects using the CALPHAD approach[J].Solid State Ionics,2004,173:17-21. |
| [5] | 夏晖,李福燊,吴卫江,杨媚,李丽芬.具有LSM致密扩散障碍层的片式极限电流型氧传感器[J].无机材料学报,2004(02):411-416. |
| [6] | 陈涛,徐政,许业文.钙钛矿锰氧化物磁制冷材料的研究[J].材料导报,2003(03):72-74. |
| [7] | R. S. Guo;Q. T. Wei;H. L. Li .Synthesis and properties of La_(0.7)Sr_(0.3)MnO_3 cathode by gel combustion[J].Materials Letters,2006(2):261-265. |
| [8] | 于东生,周震涛.La1-xSrxMnO3的制备及其电催化性能[J].稀有金属材料与工程,2005(03):463-466. |
| [9] | 张栋杰,蒋晓龙,都有为.掺杂对巨磁电阻钙钛矿La1-xAx（MnB）O3 Curie温度的影响[J].硅酸盐学报,2002(04):470-473. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%