用真空高频磁悬浮炉制备了Gd3Al2、Gd2.9Zn0.1Al2、Gd2.7Zn0.3Al2、Gd2.4Zn0.6Al2四种合金.用直接测量法测量了在1.5T磁场下这四种合金的磁热效应.结果表明,在1.5T磁场下,Gd3Al2、Gd2.9Zn0.1Al2、Gd2.7Zn0.3Al2、Gd2.4Zn0.6Al2的最大绝对温变分别为2.0K、1.4 K、1.1K和0.7K;当Zn含量为0.1时,居里温度为287K.

参考文献

[1] Kuz'min M D;Tishin A M .Magnetocaloric.part I:an introduction to various aspects of theory and practice[J].Cryogenics,1992,32(06):545.
[2] Pecharsky VK;Gschneidner KA .Giant magnetocaloric effect in Gd-5(Si2Ge2)[J].Physical review letters,1997(23):4494-4497.
[3] Cheng ZH;Di NL;Li QQ;Kou ZQ;Luo Z;Ma X;Wang GJ;Hu FX;Shen BG .Mossbauer effect probe of field-induced magnetic phase transition in LaFe13-xSix intermetallic compounds[J].Applied physics letters,2004(10):1745-1747.
[4] Tegus O .Transition-metal-based magnetic refrigerant for room-temperature application[J].Nature,2002,415:150-152.
[5] 胡凤霞,沈保根,孙继荣,王光军,成昭华.LaFe11.2Co0.7Si1.1合金在室温区的巨大磁熵变[J].物理,2002(03):139-140.
[6] 王敦辉;荫津华 等.Gd3Al2-xGax合金的磁熵研究[J].物理学报,1999,12(zk):S117-S119.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%