分别在工业纯铁和20碳钢上制备了热浸镀纯铝和稀土铝镀层,采用扫描电镜(SEM)观察了镀层横截面和表面的形貌,采用能谱仪(EDS)和电子探针(EPMA)分析了镀层横截面的稀土分布.结果表明,添加稀土热浸镀铝后,表面层厚度减少,合金层厚度增加;镀层表面比较平整、连续、无裸露点、裂纹和氧化物夹杂,且FeAl3相短而细小;稀土渗入了镀层,且分布很不均匀,在部分区域存在偏聚,表面层与合金层界面处以及齿状Fe2Al5相的边缘处和齿尖处稀土含量较高.分析了稀土对镀层厚度和组织形貌的影响及稀土的渗入机理.
参考文献
| [1] | 郑毅然,高文禄.热浸镀铝钢材的应用与发展[J].腐蚀科学与防护技术,1999(03):179-184. |
| [2] | 夏原,于升学,姚枚,李铁藩.Effect of diffusion on coating microstructure and oxidation resistance of aluminizing steel[J].中国有色金属学会会刊(英文版),2001(06):817-821. |
| [3] | Mahieu J;Maki J .Development of aluminized multi-phase steel with dual phase properties for high temperature corrosion resistance applications[J].Steel Research International,2003,74(04):225-236. |
| [4] | J.B. Wen;W. Zhang;X.Y. Li .The Influence of La on the Corrosion Resistance of Hot-Dip Aluminized Steel[J].Materials Science Forum,2005(Pt.5):3851-3854. |
| [5] | ZHANG Wei,FAN Zhi-kang,HU Peng-fei,LONG Yong-qiang,LIU Hua,WEN Jiu-ba.Effect of Rare Earth on Void Band of Diffusion Layer and Properties of Aluminized Steel[J].钢铁研究学报（英文版）,2006(05):60-64,78. |
| [6] | 杨世伟,李莉,李里,崔李萍.不锈钢热浸镀铝抗高温氧化性能研究[J].材料热处理学报,2002(04):51-53. |
| [7] | 刘邦津.钢材的热浸镀铝[M].北京:冶金工业出版社,1995 |
| [8] | 王豫;马玉明;赵明琦 .含碳量对渗铝层组织和性能的影响[J].金属热处理,1997,10:17-20. |
| [9] | 杨云;余宗森 .稀土对Zn-5%Al合金与钢板湿润性的影晌[J].中国稀土学报,1993,11(03):242-246. |
| [10] | 余瑞璜 .固体与分子经验电子理论-等效价电子假定[J].科学通报,1981,26(04):204-209. |
| [11] | 杜挺.稀土元素在金属材料中的作用与机理[J].中国有色金属学报,1996(02):13-18. |
| [12] | 刘正;吕振家 .稀土表面处理的空位机制[J].科学通报,1991,36(12):951-954. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%