以氯化镨钕溶液为原料液,分别用草酸、碳酸氢铵和碳酸钠为沉淀剂制备镨钕草酸盐和碳酸盐,在900℃～1500℃范围内不同灼烧温度下制备出镨钕二元氧化物,利用粒度仪和扫描电镜进行测试,研究了灼烧温度对稀土氧化物的粒度和形貌特征的影响;结果表明,灼烧温度的提高对中位粒径D_(50)和粒度分布R变化影响不同,改变灼烧温度对镨钕二元氧化物的形貌影响较大.
(Pr,Nd)mixed oxides were prepared by calcinating praseodymium neodymium oxalate and carbonate in the range of 900℃～1500℃ with (Pr,Nd) mixed chlorides as raw materials and oxalic acid,ammonium hydrogen carbonate and sodium carbonate as precipitants,respectively.Effecrts of calcination temperature on particle size and morphology of rare earth oxides were investigated with particle size analyzer and SEM. The results showed that change of morphology of rare earth oxides is greater than that of particle size D_(50).
参考文献
| [1] | 赵雷洪 .稀土氧化物固体碱催化剂的表面性质[J].催化学报,1996,17(03):227-231. |
| [2] | 杜森林 .熔盐电解富镨钕氧化物合成NdPrFe合金的研究[J].稀有金属,1994,18(03):167-171. |
| [3] | 顾翼东 .镨钕分离的研究Ⅱ镨钕碳酸盐在熔融体系中的热分解[J].复旦大学学报,1965,10(04):419-428. |
| [4] | 王毅军,郭军勋.晶型碳酸镨钕沉淀制备工艺的研究[J].稀有金属与硬质合金,2003(02):12-14. |
| [5] | 张亚文,严铮光,廖春生,贾江涛,严纯华.灼烧温度对单一稀土氧化物粒度、比表面积和形貌的影响（Ⅰ）[J].中国稀土学报,2001(04):378-380. |
| [6] | 中山大学金属系.稀土物理化学常数[M].北京:冶金工业出版社,1978 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%