采用硬度法、金相、X-ray 衍射、透射电镜和能谱分析等手段研究了Ag-Ti(0.05～0.61wt%Ti,下同)和Ag-Ti-Gd(0.51～1.3wt%Ti,0.09～0.46wt%Gd,下同)合金的组织、再结晶特性和相结构.结果表明:微量Ti及Ti+Gd加入Ag中,有效细化晶粒,提高晶粒组织稳定性,再结晶温度相应提高100～150℃和250℃;作者还确认了某些二相合金和三相合金;最后探讨了微量元素的作用机理.
参考文献
| [1] | 黎鼎鑫,秦国义.稀土元素对银的再结晶及晶粒组织的影响[J].贵金属,1988(04):1-9. |
| [2] | 杨玉璐 .[J].贵金属,1985,6(04):11. |
| [3] | 徐云,祁更新,邓德国.Ag-0.5Ce合金高温显微组织的稳定性[J].贵金属,1992(02):18-28. |
| [4] | 宁远涛,戴红.快速凝固Ag-Gd合金的固溶度与时效硬化[J].贵金属,1992(04):15-22. |
| [5] | 杨富陶,刘泽光,唐敏.抗时效软化的银材[J].贵金属,1992(03):22-25. |
| [6] | Murry J L;Bhansali K J .[J].Bulletin of Alloy Phase Diagrams,1983,4(02):178-183. |
| [7] | Gonde kiessler;Erich gebhardt .[J].Journal of the Less-Common Metals,1972,26:293-298. |
| [8] | Gschneidner K A;Calderwood F W .[J].Bulletin of Alloy Phase Diagrams,1985,5(06):138-139. |
| [9] | Murry J L.Binary Alloy Phase Diagrams[M].ASM International.Materials Park,1990 |
| [10] | 稀土编写组.稀土(上)[M].北京:冶金工业出版社,1987 |
| [11] | Gallagher P C .[J].Metallurgical Transactions,1970,1:2429. |
| [12] | Howie A;Swan P R .[J].Philosophical Magazine,1961,6:125. |
| [13] | Thomton P R;Michell T F;Hirsch P B .[J].Philosophical Magazine,1962,7:1349. |
| [14] | 胡庚祥;钱苗根.金属学[M].上海:上海科学技术出版社,1980:303. |
| [15] | Zener C.[J].Transactions of the Metallurgical Society of AIME,1948:175. |
| [16] | Gladman T .[Z].Proc.Roy.Soc,1966. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%