制备了具有不同Ag含量的Cu-Ag合金及其原位纤维复合材料,增加Ag含量可以细化铸态组织和Ag纤维尺寸,增大合金的极限拉伸强度和电阻率.但当Ag含量＞20%,这种对组织细化和性能影响的趋势减小.研究了凝固条件、微量稀土添加和中间热处理等冶金学因素对低Ag含量的Cu-Ag合金及其原位纤维复合材料的结构和性能的影响,获得了具有拉伸强度σb＞1.5GPa和导电率γ＞60%IACS的Cu-Ag合金原位纤维复合材料.讨论了大变形Cu-Ag合金原位纳米纤维复合材料所显示的两阶段应变强化效应及其机制.
参考文献
| [1] | Sakai Y;Inoue K;Asano T et al.Development of high strength high conductivity Cu-Ag alloy for high field pulsed magnet use[J].Applied Physics Letters,1991,59(23):2965-2967. |
| [2] | Sakai Y.;Inoue K. .Development of a high strength, high conductivity copper-silver alloy for pulsed magnets[J].IEEE Transactions on Magnetics,1992(1):888-891. |
| [3] | Dew-Hughes D .High strength conductor for pulsed magnets[J].Materials Science and Engineering,1993,A168(01):35-40. |
| [4] | Y. SAKAI;K. INOUE;H. MAEDA .NEW HIGH-STRENGTH, HIGH-CONDUCTIVITY Cu-Ag ALLOY SHEETS[J].Acta Metallurgica et Materialia,1995(4):1517-1522. |
| [5] | Y.SAKAI;H.-J.SCHNEIDER-MUNTAU .ULTRA-HIGH STRENGTH, HIGH CONDUCTIVITY Cu-Ag ALLOY WIRES[J].Acta materialia,1997(3):1017-1023. |
| [6] | 张晓辉,宁远涛,李永年,戴红,杨家明.大变形Cu-10Ag原位纤维复合材料的结构和性能[J].中国有色金属学报,2002(01):115-119. |
| [7] | 宁远涛,张晓辉,张婕.大变形Cu-Ag合金原位纤维复合材料的稳定性[J].中国有色金属学报,2005(04):506-512. |
| [8] | 宁远涛,张晓辉,张婕.大变形Cu-10Ag原位纳米纤维复合材料[J].稀有金属材料与工程,2005(12):1930-1934. |
| [9] | 宁远涛,张晓辉,吴跃军.Cu-Ag合金原位纤维复合材料的形变特征[J].贵金属,2006(03):1-6. |
| [10] | 宁远涛,张晓辉,秦国义,张婕.不同凝固条件制备的Cu-Ag合金原位纤维复合材料的结构与性质[J].贵金属,2005(03):39-50. |
| [11] | Benghalem A;Morris D C .Microstructure and strength of wire-draw Cu-Ag filamentary composites[J].Acta Metallurgica,1997,45(01):397. |
| [12] | Frommeyer G;Wassenmann G .Microstructure and anomalous mechanical properties of in situ produced silver-copper composite wire[J].Acta Metallurgica,1975,23:1353. |
| [13] | 宁远涛,张晓辉,吴跃军.Cu-Ag合金原位纤维复合材料的应变强化效应[J].中国有色金属学报,2007(01):68-74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%