用溶液涂刷热解法制备了RuO2-IrO2/Ta超级电容器薄膜电极材料.X射线衍射(XRD)、扫描电镜(SEM)对薄膜电极材料的结构和形貌的分析表明制备的电极材料具有纳米尺度和多孔结构.热分析表明(RuO2-IrO2)·nH2O/Ta的结晶转化温度约为327℃.在频率为100 Hz时经320℃/30 min处理涂刷5层的热分解法制备的电极在浓度为37％的硫酸溶液中获得最大电容为55mF/143 mm2.
参考文献
| [1] | 唐致远,耿新,王占良,徐国祥.金属氧化物电化学电容器[J].化学通报,2003(01):33-38. |
| [2] | 汪形艳,王先友,黄伟国.超级电容器电极材料研究[J].电池,2004(03):192-193. |
| [3] | Zheng J P;Xin Y .Characterization of RuO2 @ xH2O with various water contents[J].Journal of Power Sources,2002,110:86-90. |
| [4] | Sujit Kumar Mondal;N. Munichandraiah .Anodic deposition of porous RuO_2 on stainless steel for supercapacitor studies at high current densities[J].Journal of Power Sources,2008(1):657-663. |
| [5] | David A.Evans.最小的大容量电容器--Evans混合电容器[J].电子元件与材料,2002(10):13-15,18. |
| [6] | Chi-Chang Hu;Chen-Ching Wang;Kuo-Hsin Chang .A comparison study of the capacitive behavior for sol-gel-derived and co-annealed ruthenium-tin oxide composites[J].Electrochimica Acta,2007(7):2691-2700. |
| [7] | Gujar TP;Shinde VR;Lokhande CD;Kim WY;Jung KD;Joo OS .Spray deposited amorphous RUO2 for an effective use in electrochemical supercapacitor[J].Electrochemistry communications,2007(3):504-510. |
| [8] | 刘泓,甘卫平,黄波,刘继宇,李祥,郑峰.掺锡氧化钌超级电容器薄膜电极的研制[J].稀有金属材料与工程,2011(01):115-120. |
| [9] | 甘卫平,黎小辉,欧定斌,覃政辉.退火温度对钽基RuO2·nH2O电沉积薄膜电容性能的影响[J].中南大学学报（自然科学版）,2006(04):660-664. |
| [10] | 倪月琴;臧璟龄;李小竹 等.沉积氯铱酸的y-Al2O3的表面性质[J].催化学报,1982,3(02):81-86. |
| [11] | 罗洪原;初玉芝;徐翠兰 等.CO在lr/Al2O3催化剂上的吸附及与O相互作用的IR研究[J].催化学报,1990,11(04):284-289. |
| [12] | 徐艳.电化学电容器钽基氧化钌电极的制备和性能研究[M].长沙:国防科技大学出版社,2005:1-72. |
| [13] | 王晓峰,尤政,阮殿波.溶胶凝胶方法制备纳米氧化钌的超电容特性[J].化学物理学报,2006(04):341-346. |
| [14] | Cullity B D.Elements of X-ray Diffraction[M].New Jersey:Addison-Wesley publishing company,1978:448-451. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%