锌镍合金镀层由于其优良的耐蚀性而广泛应用于汽车、航空、电子等行业.在此研究了氯化物-硫酸盐体系的锌镍合金电镀.研究了Ni2+/Zn2+重量比、电流密度和温度对镀层镍含量的影响,优选出一种较为理想的工艺.此外,通过阴极极化曲线和循环伏安曲线的测量研究了锌镍共沉积的电化学行为及光亮剂的作用.实验发现,光亮剂的存在能提高锌镍共沉积的阴极极化,表明其阻化作用使得锌镍合金镀层结晶细致,从而获得光亮镀层.
参考文献
| [1] | Abd El Rehim S S;Fouad E E;Abd El Wahab et al.Electroplating of Zinc-Nickel binary alloys[J].Electrochimica Acta,1996,41(09):1413-1418. |
| [2] | Fratesi R;Roventi G .Electrodeposition of Zinc-Nickel alloy coatings from a chloride bath containing[J].New Journal of Chemistry,1992,22:657. |
| [3] | Karwas C;Hepel T .Influence of Boric Acid on Elctrodeposition and Stripping of Ni-Zn Alloys[J].Journal of the Electrochemical Society,1988,135(04):839. |
| [4] | Fabri Miranda F J;Barcia O E;Diaz S L et al.Electrodeposition of Zn-Ni alloys in sulfate electrolytes[J].Electrochimica Acta,1996,41(7/8):1041-1049. |
| [5] | Fabri Miranda F J;Barcia O E;Diaz S L et al.Electrodeposition of Zn-Ni alloys in sulfate electrolytes[J].Journal of the Electrochemical Society,1997,144(10):3441. |
| [6] | Lin Y P;Robert S J .Elctrodepositon of Corrosion-Resistant Ni-Zn alloys[J].Journal of Elcetrochem Soc,1993,140(05):1299-1303. |
| [7] | 倪步高.从氯化钾镀液中电镀光亮锌镍合金[J].材料保护,1992(09):32. |
| [8] | 熊刚;邹群;蔡群英.络合剂对锌-镍合金层中镍含量的影响[A].武汉:中国表面工程协会电镀分会,1994:58-60. |
| [9] | 曾华梁;李春梅;梁京华.电镀锌镍合金代镉工艺的研究[A].南京:中国电镀协会学工作委员会,1990:85-87. |
| [10] | 屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:212-228. |
| [11] | Huang C H .Duplex Zinc-Nickel Alloy Electrodeposits[J].Plating and surface finishing,1989,76(12):64-67. |
| [12] | 周绍民.金属电沉积-原理与研究方法[M].上海:上海科学技术出版社:1987. |
| [13] | 左正忠;陈永言.WD 87型氯化物镀锌光亮剂的研究[J].表面技术,1989(02):23-28. |
| [14] | Fletcher S .Some new formulae applicable to eletrochemical nucleation/growth/collision[J].Electrochimica Acta,1983,28:917. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%