铝铜合金由于重量轻、机械强度高而得到广泛应用。然而，由于铜的存在使铝铜合金的演技氧化变得困难。分析了铜含量对铝铜合金阳极氧化的不良影响，并总结了集中改进措施如电解液成分、温度、搅拌以及外加电流方式等。
Aluminum-copper alloy has been widely adopted for its low weight and high mechanical strength, but the existence of copper makes the anodizing of aluminum-copper alloy difficult. Herein, the detrimental effects of copper on anodic oxidation of aluminum-copper alloy were discussed, and modified measures were introduced such as electrolyte composition, temperature, agitation and the way of imposed current.
参考文献
| [1] | 张绍恭.轻合金表面处理[M].上海:科学技术编译馆,1964:64. |
| [2] | 李华 .硬质阳极氧化膜层厚度控制[J].电镀与环保,1997,17(05):21. |
| [3] | 凯普 .[J].电镀与环保,1992,12(02):14. |
| [4] | 周谟银.[J].上海电镀,1984(03):8. |
| [5] | 航空航天表面技术会.腐蚀与防护技术[M].南昌:南昌航空工业学院出版社,1992:174. |
| [6] | 《电镀手册》编写组.电镀手册[M].北京:国防工业出版社,1997:554. |
| [7] | 张玉麟.航空制造工程手册:表面处理分册[M].北京:航空工业出版社,1993:202-203. |
| [8] | 曾华梁.电解和化学转化膜[M].北京:中国轻工业出版社,1987:323. |
| [9] | 曾凌三.铝合金交流电氧化工艺的研究[J].电镀与精饰,1994(01):4. |
| [10] | 张宏祥.铝合金脉冲硬质阳极氧化的研究[J].电镀与精饰,1986(02):3. |
| [11] | 贝红斌;朱祖芳 .脉冲氧化与恒流氧化的氧化过程和氧化膜性能[J].电镀与环保,1996,16(04):25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%