介绍了两步法钢铁钼系无毒常温发黑工艺。与高温碱性发黑相比,常温发黑膜的结合力和耐蚀性较差,发黑液稳定性差。在此探讨了常温钢铁钼系发黑液的维护方法,采用调整酸度和密封保存方式可延长发黑液的使用寿命,再生处理可降低成本、减轻环境污染。此外,提出了一种新型低毒钝化工艺。大大提高了发黑膜的附着力和耐蚀性。

Two step molybdenum-containing non-toxic blackening of iron andsteel was described. Compared to alkaline blackening of iron and steel at high temperature, blackening at room temperature has weaknesses such as poor adhesion and corrosion resistance, low stabilty. Maintenance of room temperature blackening solution was investigated. Service life of blackening solution can be extended by adjustment of solution acidity and closed storage. Production cost and environment pollution can be reduced by renewal of the blackening solution. In additionl, a new low toxic passivation process was advanced which improved the adhesion and corrosion resistance of blackening film greatly.

参考文献

[1] Paul Jarvl;Orange;Conn .Room Temperature Blackening Solution[P].U S P: 4 728 365,1986.
[2] 王翎;张广遇 .常温发黑的污染控制[J].电镀与环保,1995,15(06):27-28.
[3] 杨勤俭.我国常温发黑技术的现状和发展[J].电镀与精饰,1996(03):30.
[4] 邓立元,周书天.两步法钼系钢铁无毒常温发黑的研究[J].湘潭大学自然科学学报,2000(02):78-81.
[5] 郭良生,黄霓裳.钢铁室温除油除锈二合一处理剂[J].材料保护,1992(02):35.
[6] 周书天;杨润昌;傅志强 .Cu-S钢铁无毒化学发黑液[J].电镀与涂饰,1997,16(01):18-21.
[7] 周长虹;罗和平;李贤成 .双氧水在表面处理中的作用[J].电镀与环保,1995,15(06):9-11.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%