为了提高Zn-Fe合金镀层耐蚀性,采用非银盐发黑剂,结合磷化工艺,并加入适当的添加剂及辅助成膜剂,研制出了一种新的Zn-Fe合金镀层黑色钝化工艺.该钝化液中铬酸含量低,污染小,且化学性能稳定,使用寿命长.详细研究了钝化液中各组分对钝化膜成膜及其耐蚀性的影响,从而确定了最佳的钝化液组成.研究结果表明,采用该种钝化液获得的钝化膜油黑发亮,色泽均匀,耐蚀性及耐磨性好,附着力强.
参考文献
| [1] | 李华为;刘云丽;车承焕 .电镀铁系锌基合金的现状分析[J].电镀与环保,1998,18(03):16-18. |
| [2] | David Crotty .Zinc Alloy Plating for the Automotive Industry[J].Metal finishing,1996(9):54,56-58-0. |
| [3] | 小谷勇;野田裕臣 .The operation of zinc alloy plating in Japan[J].表面技术(日本),1996,47(10):11-13. |
| [4] | Roper M E;Grady J O .Zinc alloy coating-a European perspective[J].Transactions of the Institute of Metal Finishing,1996,74(04):3-6. |
| [5] | Barnes C;Ward J J .Trivalent chromium passivated processes[J].Transactions of the Institute of Metal Finishing,1982,60(01):104-111. |
| [6] | Wilcox G D;Wharton J A .A review of chromate free passivation treatments for zinc and zinc alloys[J].Transactions of the Institute of Metal Finishing,1997,75(06):B140. |
| [7] | 卢锦堂,宋进兵,陈锦虹,许乔瑜,孔纲.无铬钝化的研究进展[J].材料保护,1999(03):24-26. |
| [8] | Wharton J A;Wilcox G D;Baldwin K R .Non-chromate conversion coating treatment for electrodeposited zinc-nickel alloys[J].Transactions of the Institute of Metal Finishing,1996,74(06):210-215. |
| [9] | Cowicson D R;Scholefield A R .Passivation of tin-zinc alloy coated steel[J].Transactions of the Institute of Metal Finishing,1985,63(02):56-59. |
| [10] | 周金宝 .镀锌层无铬钝化工艺的新进展[J].电镀与环保,1996,11(05):7-11. |
| [11] | 韩克平.镀锌层表面硅酸盐防腐膜的研究[J].腐蚀科学与防护技术,1997(02):167. |
| [12] | 张景双,安茂忠,杨哲龙,屠振密.电镀锌及锌合金镀层钝化处理的应用与发展[J].材料保护,1999(07):14-16. |
| [13] | 黄盛朗 .镀锌及锌合金发展综述[J].电镀与环保,1996,16(02):3-6. |
| [14] | 张安富.镀锌及锌合金着黑色新工艺[J].电镀与精饰,1996(01):19. |
| [15] | HB5062-1977.HB5062-1977.钢铁化学氧化(发蓝)点滴法耐蚀标准[S]. |
| [16] | GB /9791-1988.GB/9791-1988.锌和镉上铬酸盐转化膜试验方法[S]. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%